The aim of this in vitro study was to evaluate and compare the color stability of different esthetic restorative materials (one microfilled composite, one nanofilled composite, one nanoceramic composite, one microfilled hybrid composite, one microfilled hybrid composite, one nanohybrid Ormocer based composite and one supra-nano spherical hybrid composite) after exposure to different staining solutions (physiological saline, red wine, coffee). All materials were prepared and polymerized into silicon rings (2 mm × 6 mm × 8 mm) to obtain specimens identical in size. Thirty cylindrical specimens of each material were prepared. Specimens were immersed in staining solutions (physiological saline, coffee and red wine) over a 28-day test period. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. The Shapiro–Wilk test and ANOVA were applied to assess significant differences among restorative materials. A paired t-test was applied to test which CIE L*a*b* parameters significantly changed after immersion in staining solutions. All restorative materials showed significant color differences after immersion in coffee. Coffee caused a significant color change in all types of tested composite resins. Only Filtek Supreme XTE demonstrated a staining susceptibility to red wine; no other significant differences among the materials were demonstrated. Long-term exposure to some food dyes (coffee in particular) can significantly affect the color stability of modern esthetic restorative materials regardless of materials’ different compositions.

The aim of the present study was to evaluate and compare the cytotoxic effects of eight composite resins on immortalized human gingival fibroblasts. Composite resins were eluted in cell culture medium for 48 or 72 h at 37 °C. Immortalized human gingival fibroblast-1 (HGF-1) cell lines were seeded in 96-well (1 × 10⁴) plates and incubated for 24 h at 37 °C with the obtained extraction medium. The percentage of viable cells in each well (MTT test) was calculated relative to control cells, which were set to 100%. Data observed were not normally distributed, and nonparametric statistical methods were used for statistical analysis. The Wilcoxon test was used for intragroup comparison, and the Kruskal–Wallis test was used for intergroup multiple comparisons. Significance value was set as p < 0.05. All materials tested showed cytotoxic effects on gingival fibroblasts, recordable as noncytotoxic, mildly cytotoxic or severely cytotoxic, depending on the percentage of cell viability. The Wilcoxon test for intragroup comparison showed that the percentage of viable cells decreased significantly for extracts, for all composite resins tested. The composite resins contained monomers that displayed cytotoxic properties. BisGMA, TEGDMA and UDMA had inhibitory effects and induced apoptotic proteins in pulp fibroblast. Composite resins that contained lower percentages of unbound free monomers—and that released less ions—possessed superior biocompatibility in vitro.

Nickel-titanium (NiTi) instruments are commonly used for shaping the root canal system in endodontic practice. They are more flexible and have better cutting efficiency than conventional stainless steel files. The superelasticity of NiTi rotary files allows the clinicians to produce the desirable tapered root canal form with a reduced tendency to canal transportation and instrument fracture. HyFlex CM instruments are new NiTi rotary instruments with shape memory produced by an innovative methodology (patent pending) that uses a complex heating and cooling treatment that controls the material’s memory. The aim of the present study was to compare the cleaning efficacy of two conventional (Mtwo, Revo-S) Ni-Ti rotary instruments with HyFlex CM. 30 single-rooted freshly extracted teeth were divided into three groups. Root canals were shaped with three NiTi instruments (Mtwo, Revo-S and HyFlex CM) using 5.25% NaOCl and 17% EDTA solutions. Specimens were fractured longitudinally and prepared for SEM analysis at standard magnification of 1000×. The presence/absence of debris smear layer and the presence/absence of smear layer at coronal, middle, and apical third of each canal were evaluated using a 5-step scale for scores. Numeric data were analyzed using Kruskall-Wallis and Mann-Whitney U statistical tests and significance was predetermined at P < 0.05. This study revealed significant differences among the various groups. Despite some minor differences, all instruments removed smear layer and debris produced during instrumentation. HyFlex CM seem to be not so effective in promoting cleanliness of root canal walls and in removing smear layer from dentine if compared to Mtwo and Revo-S.

This study evaluated the root canal dentine surface by scanning electron microscope (SEM) after shaping with two reciprocating single-file NiTi systems and two rotating single-file NiTi systems, in order to verify the presence/absence of the smear layer and the presence/absence of open tubules along the walls of each sample; Forty-eight single-rooted teeth were divided into four groups and shaped with OneShape (OS), F6 SkyTaper (F6), WaveOne (WO) and Reciproc and irrigated using 5.25% NaOCl and 17% EDTA. Root canal walls were analyzed by SEM at a standard magnification of 2500×. The presence/absence of the smear layer and the presence/absence of open tubules at the coronal, middle, and apical third of each canal were estimated using a five-step scale for scores. Numeric data were analyzed using Kruskal-Wallis and Mann-Whitney U statistical tests and significance was predetermined at P < 0.05; The Kruskal-Wallis ANOVA for debris score showed significant differences among the NiTi systems (P < 0.05). The Mann-Whitney test confirmed that reciprocating systems presented significantly higher score values than rotating files. The same results were assessed considering the smear layer scores. ANOVA confirmed that the apical third of the canal maintained a higher quantity of debris and smear layer after preparation of all the samples; Single-use NiTi systems used in continuous rotation appeared to be more effective than reciprocating instruments in leaving clean walls. The reciprocating systems produced more debris and smear layer than rotating instruments.

Consumption of acidic beverages and foods could provoke erosive damage, both for teeth and for restorative materials. Temperatures of consumption could influence the erosive effects of these products. The aim of this in vitro study is to assess the influence of an acidic challenge on the weight loss of different restorative materials. Resin composites and glass-ionomer cements (GIC) were tested. The medium of storage was Coca-Cola (Coca-Cola, Coca-Cola Company, Milano, Italy) at two different temperatures, 4 and 37 °C, respectively for Group A and Group B. For each group, nine specimens were prepared for each material tested. After 7 days, weight was assessed for each sample, and the percentage weight loss was calculated. For all the resin composites (Groups 1–13), no significant weight losses were noticed. (<1%). Conversely, GICs (Groups 14 and 15) showed significant weight loss during the acidic challenge, which was reduced in the case of these materials that included a protective layer applied above. Significant differences were registered with intra-group analysis; weight loss for specimens immersed in Coca Cola at 37 °C was significantly higher for almost all materials tested when compared to specimens exposed to a cooler medium. In conclusion, all the resin composites showed reliable behaviour when exposed to acidic erosion, whereas glass-ionomer cements generally tended to solubilize.

Composite resins are commonly used in dentistry for direct restorations. The color stability of these materials still represents a major concern for both the clinician and the patient. In recent years, ozone therapy has been extensively used in dentistry to manage wounds healing, dental caries, oral lichen planus, gingivitis and periodontitis, halitosis, osteonecrosis of the jaw, post-surgical pain, plaque and biofilms, root canal treatment, dentin hypersensitivity, temporomandibular joint disorders, and teeth whitening. To date, several studies have evaluated the bleaching effect exerted by ozone on natural teeth, but no studies have been conducted to determine the effect on the color of composite resins. The aim of the present study is to determine whether ozonized oils/gels could determine a color change on composite resin. A total of 40 discs of an A3 shade restorative composite were divided into two groups, respectively exposed to a pigmentation treatment consisting of 10 applications of 10 min each of a 1% chlorhexidine-based gel (trial group) and to storage into physiological solution (control group). The samples of both groups were respectively subdivided into four subgroups which underwent four different protocols, three of which were based on the exposure to different ozonized products and the latter representing the control. A colorimetric analysis with the CIELAB method was conducted with the following timing: after 24 h of storage in physiological solution (before the experimental procedures) (T0), after the subdivision into groups A and B (corresponding to the pigmentation for samples of group A and storage in physiological solution for samples of group B) (T1), and after subdivision into subgroups 1–4 (corresponding to the application of the ozonized products vs. control) (T2). No statistically significant difference was found between the samples at T0. The 20 samples of group A, exposed to the colorant agent, underwent a color change from T0 to T1, whereas the 20 samples exposed to the physiologic solution did not undergo any significant color change. A positive but moderate influence was assessed for E and L values, whereas no significant change occurred for A and B values. Therefore, dental ozonized oils/gels could be valuable in restorative dentistry as bleaching agents of resin composites exposed to discoloration, an alternative to the traditional hydrogen peroxide and carbamide peroxide, but further studies are required to confirm these findings.