Single-atom catalysts with full utilization of metal centers can bridge the gap between molecular and solid-state catalysis. Metal-nitrogen-carbon materials prepared via pyrolysis are promising single-atom catalysts but often also comprise metallic particles. Here, we pyrolytically synthesize a Co–N–C material only comprising atomically dispersed cobalt ions and identify with X-ray absorption spectroscopy, magnetic susceptibility measurements and density functional theory the structure and electronic state of three porphyrinic moieties, CoN₄C₁₂, CoN₃C_10,porp and CoN₂C₅. The O₂ electro-reduction and operando X-ray absorption response are measured in acidic medium on Co–N–C and compared to those of a Fe–N–C catalyst prepared similarly. We show that cobalt moieties are unmodified from 0.0 to 1.0 V versus a reversible hydrogen electrode, while Fe-based moieties experience structural and electronic-state changes. On the basis of density functional theory analysis and established relationships between redox potential and O₂-adsorption strength, we conclude that cobalt-based moieties bind O₂ too weakly for efficient O₂ reduction.

Oxygen electrochemistry is at the core of several emerging energy conversion technologies. The role of carbon nanostructures in the electrocatalysis of the oxygen reduction reaction is not well understood. Herein we report an investigation of the role of graphitic edges in oxygen electrochemistry. A new synthetic method was used to create all-carbon model electrode materials with controlled morphology. Electron microscopy results show that synthesized materials possess a high density of graphitic edges. Electrochemical intercalation experiments however indicate that the density of electroactive edges does not correlate positively with microscopy results. The materials were then characterized as electrodes for the oxygen reduction reaction in alkaline media. Results suggest that electrochemical determinations of edge and defect density more accurately predicts electrocatalytic activity thus suggesting that in situ characterization techniques are needed to understand the carbon/electrolyte interface.

N-doped carbon nanomaterials have received increased attention from electrochemists due to their applications in the metal-free electrocatalysis of important redox processes. In this work, a series of graphitized undoped and nitrogen-doped carbon electrodes prepared by thermal annealing of sputtered amorphous carbon films were prepared and characterized using a combination of X-ray photoelectron spectroscopy and Raman spectroscopy. Adsorption of the surface-sensitive redox probe dopamine at each electrode surface was then studied using cyclic voltammetry and the results correlated to the physico-chemical characterisation. Results indicate that dopamine adsorption is influenced by both the nitrogen surface chemistry and the degree of graphitization of the carbon scaffold. N-doping, with predominantly graphitic-N sites, was found to increase adsorption of dopamine more than 6 fold on carbon surfaces when the introduction of N atoms did not result in substantial alterations to the sp² network. However, when an identical type and level of N-doping is accompanied by a significant increase in disorder in the carbon scaffold, adsorption is limited to levels comparable to those of nitrogen-free carbon. Density functional theory studies of dopamine adsorption on graphene and N-doped graphene model surfaces showed that dopamine interacts via π-stacking at the graphene surface. The Gibbs free energy of adsorption on N-doped graphenes were estimated at 12-13 kcal mol^-1, and found to be approximately twice that of undoped graphenes. Results suggest that chemical changes resulting from N-doping enhance adsorption; however, high coverage values depend on the availability of sites for π-stacking. Therefore, the structurally disruptive effects of N-incorporation can significantly depress the dopamine response by limiting the availability of basal sites, ultimately dominating the overall electrochemical response of the carbon electrode.

Research with proton exchange membrane fuel cells has demonstrated their potential as important providers of clean energy. The commercialization of this type of fuel cell needs a breakthrough in the electrocatalyst technology to reduce the relatively large amount of noble metal platinum used with the present carbon based substrates. We have recently examined suitably sized silicon carbide (SiC) particles as catalyst supports for fuel cells based on the stable chemical and mechanical properties of this material. In the present study, we have continued our work with studies of the oxygen reduction and methanol oxidation reactions of SiC supported catalysts and measured them against commercially available carbon based catalysts. The deconvolution of the hydrogen desorption signals in CV cycles shows a higher contribution of Pt (110) and Pt (111) peaks compared to Pt (100) for SiC based supports than for carbon based commercial catalysts, when HClO₄ is used as an electrolyte. The Pt (110) and Pt (111) facets are shown to have higher electrochemical activities than Pt (100) facets. To the best of our knowledge, methanol oxidation studies and the comparison of peak deconvolutions of the H desorption region in CV cyclic studies are reported here for the first time for SiC based catalysts. The reaction kinetics for the oxygen reduction and for methanol oxidation with Pt/SiC are observed to be similar to the carbon based catalysts. The SiC based catalyst shows a higher specific surface activity than BASF (Pt/C) for methanol oxidation and oxygen reduction while the mass activity values are comparable.