A novel high-performance magnetorheological material, named as magnetorheological plastomer (MRP), was developed by dispersing iron particles into a plastic polyurethane (PU) matrix. The dynamic properties (including storage modulus and loss factor) of the MRP material were systematically tested and the influences of the iron particle content and magnetic field were analyzed. It is found that the anisotropic MRP product with 80% iron particle weight fraction (A-MRP-80), shows a high dynamic property: the maximum magneto-induced storage modulus is 6.54 MPa; the relative MR effect reaches as high as 532%; the loss factor can be reduced to 0.03 by adjusting magnetic field. This kind of MRP shows a much higher magnetorheological performance than the previously reported magnetorhelogical elastomer (MRE). The mechanism for its high MR performance was proposed and the influence of the iron particle distribution and temperature on the dynamic properties were discussed.

Recently, owing to their special spatial structures, peptide-based macrocycles have shown tremendous promise and aroused great interest in multidisciplinary research ranging from potent antibiotics against resistant strains to functional biomaterials with novel properties. Besides traditional monocyclic peptides, many fascinating polycyclic and remarkable higher-order cyclic, spherical and cylindric peptidic systems have come into the limelight owing to breakthroughs in various chemical (e.g., native chemical ligation and transition metal catalysis), biological (e.g., post-translational enzymatic modification and genetic code reprogramming), and supramolecular (e.g., mechanically interlocked, metal-directed folding and self-assembly via noncovalent interactions) macrocyclization strategies developed in recent decades. In this tutorial review, diverse state-of-the-art macrocyclization methodologies and techniques for peptides and peptidomimetics are surveyed and discussed, with insights into their practical advantages and intrinsic limitations. Finally, the synthetic-technical aspects, current unresolved challenges, and outlook of this field are discussed.

This work illustrates a “soft‐toughness” coupling design method to integrate the shear stiffening gel (SSG), natural leather, and nonwoven fabrics (NWF) for preparing leather/MXene/SSG/NWF (LMSN) composite with high anti‐impact protecting, piezoresistive sensing, electromagnetic interference (EMI) shielding, and human thermal management performance. Owing to the porous fiber structure of the leather, the MXene nanosheets can penetrate leather to construct a stable 3D conductive network; thus both the LM and LMSN composites exhibit superior conductivity, high Joule heating temperature, and an efficient EMI shielding effectiveness. Due to the excellent energy absorption of the SSG, the LMSN composites possess a huge force‐buffering (about 65.5%), superior energy dissipation (above 50%), and a high limit penetration velocity of 91 m s⁻¹, showing extraordinary anti‐impact performance. Interestingly, LMSN composites possess an unconventional opposite sensing behavior to piezoresistive sensing (resistance reduction) and impact stimulation (resistance growing), thus they can distinguish the low and high energy stimulus. Ultimately, a soft protective vest with thermal management and impact monitoring performance is further fabricated, and it shows a typical wireless impact‐sensing performance. This method is expected to have broad application potential in the next‐generation wearable electronic devices for human safeguarding.