This comprehensive review focuses on polyetheretherketone (PEEK), a synthetic thermoplastic polymer, for applications in dentistry. As a high-performance polymer, PEEK is intrinsically robust yet biocompatible, making it an ideal substitute for titanium—the current gold standard in dentistry. PEEK, however, is also inert due to its low surface energy and brings challenges when employed in dentistry. Inert PEEK often falls short of achieving a few critical requirements of clinical dental materials, such as adhesiveness, osseoconductivity, antibacterial properties, and resistance to tribocorrosion. This study aims to review these properties and explore the various surface modification strategies that enhance the performance of PEEK. Literatures searches were conducted on Google Scholar, Research Gate, and PubMed databases using PEEK, polyetheretherketone, osseointegration of PEEK, PEEK in dentistry, tribology of PEEK, surface modifications, dental applications, bonding strength, surface topography, adhesive in dentistry, and dental implant as keywords. Literature on the topics of surface modification to increase adhesiveness, tribology, and osseointegration of PEEK were included in the review. The unavailability of full texts was considered when excluding literature. Surface modifications via chemical strategies (such as sulfonation, plasma treatment, UV treatment, surface coating, surface polymerization, etc.) and/or physical approaches (such as sandblasting, laser treatment, accelerated neutral atom beam, layer-by-layer assembly, particle leaching, etc.) discussed in the literature are summarized and compared. Further, approaches such as the incorporation of bioactive materials, e.g., osteogenic agents, antibacterial agents, etc., to enhance the abovementioned desired properties are explored. This review presents surface modification as a critical and essential approach to enhance the biological performance of PEEK in dentistry by retaining its mechanical robustness.

The study of regenerative dentistry receives a fast growing interest. The potential ability of the dentin-pulp complex to regenerate is both promising and perplexing. To answer the challenging nature of the dental environment, scientists have developed various combinations of biomaterial scaffolds, stem cells, and incorporation of several growth factors. One of the crucial elements of this tissue engineering plan is the selection and fabrication of scaffolds. However, further findings suggest that cell behavior hugely depends on mechanical signaling. Nanotopography modifies scaffolds to alter cell migration and differentiation. However, to the best of the author's knowledge, there are very few studies addressing the correlation between nanotopography and dentin-pulp complex regeneration. Therefore, this article presents a comprehensive review of these studies and suggests a direction for future developments, particularly in the incorporation of nanotopography design for dentin-pulp complex regeneration.

Collagen (Col) is a naturally available material and is widely used in the tissue engineering and medical field owing to its high biocompatibility and malleability. Promising results on the use of Col were observed in the periodontal application and many attempts have been carried out to inculcate Col for gingival recession (GR). Col is found to be an excellent provisional bioscaffold for the current treatment in GR. Therefore, the aim of this paper is to scrutinize an overview of the reported Col effect focusing on in vitro, in vivo, and clinical trials in GR application. A comprehensive literature search was performed using EBSCOhost, Science Direct, Springer Link, and Medline & Ovid databases to identify the potential articles on particular topics. The search query was accomplished based on the Boolean operators involving keywords such as (1) collagen OR scaffold OR hybrid scaffold OR biomaterial AND (2) gingiva recession OR tissue regeneration OR dental tissue OR healing mechanism OR gingiva. Only articles published from 2015 onwards were selected for further analysis. This review includes the physicochemical properties of Col scaffold and the outcome for GR. The comprehensive literature search retrieved a total of 3077 articles using the appropriate keywords. However, on the basis of the inclusion and exclusion criteria, only 15 articles were chosen for further review. The results from these articles indicated that Col promoted gingival tissue regeneration for GR healing. Therefore, this systematic review recapitulated that Col enhances regeneration of gingival tissue either through a slow or rapid process with no sign of cytotoxicity or adverse effect.

One of the major challenges in the development of scaffold for nerve regeneration is enhancing mechanical strength of the material to avoid the scaffold to rapidly degrade during regeneration process in nerve system. The aim of this study was to reveal the effect of freeze-thaw to the properties of gelatin-carbonated hydroxy apatite (CHA) membrane in two ratios 7 to 3 and 6 to 4 for gelatin to CHA respectively. Some variations of freeze-thaw cycles were applied for both ratios, which is referred for its biocompatibility in cells.The CHA was synthesized by wet precipitating method of calcium hydroxide and phosphoric acid in gelatin solution at room temperature and open system. The X-Ray Diffraction (XRD) and FTIR analysis was conducted to confirm the formation of type-B CHA in gelatin matrix. The resulted membrane was then subject for membrane characterization.It was known from the study that freeze-thaw treatment during membrane fabrication affects several properties of the membrane. Platelet loading capability decreased when freeze-thaw cycles increased. Meanwhile, the platelet was released more rapidly by freeze-thawed gelatin-CHA membrane compared to non-freeze-thawed one. The degradation percentage of the membrane decreased with the increasing freeze-thaw cycles, showing 4 hours slower degradation in the freeze-thawed membrane compared to the unfreeze-thawed one.Furthermore, it was observed that freeze-thaw improved the tensile strength of the membrane and the modulus elasticity increased simultaneously. Moreover, in general it was observed from this study that freeze-thaw treatment did not affect permeability of the membranes towards glucose transport.