P-i-n geometry perovskite solar cells (PSCs) offer simplified fabrication, greater amenability to charge extraction layers, and low-temperature processing over n-i-p counterparts. Self-assembled monolayers (SAMs) can enhance the performance of p-i-n PSCs but ultrathin SAMs can be thermally unstable. We report a thermally robust hole-selective layer comprised of nickel oxide (NiO _x ) nanoparticle film with a surface-anchored (4-(3,11-dimethoxy-7H-dibenzo[c,g]carbazol-7-yl)butyl)phosphonic acid (MeO-4PADBC) SAM that can improve and stabilize the NiO _x /perovskite interface. The energetic alignment and favorable contact and binding between NiO _x /MeO-4PADBC and perovskite reduced the voltage deficit of PSCs with various perovskite compositions and led to strong interface toughening effects under thermal stress. The resulting 1.53–electron-volt devices achieved 25.6% certified power conversion efficiency and maintained >90% of their initial efficiency after continuously operating at 65 degrees Celsius for 1200 hours under 1-sun illumination.

Photoluminescence of simple arylbenzenes with ready synthetic accessibility is enhanced by two orders of magnitude through aggregate formation; viscosity and temperature effects indicate that the emission enhancement is due to the restriction of their intramolecular rotations in the solid state.

The review reports the recent progress in organic second-order and third-order nonlinear optical materials in the Jen group.