The increasing demand for aluminum in conjunction with the limited available bauxite deposits in Europe results in the dire need for the evaluation of alternative raw materials for the whole value chain of alumina production. The present paper focuses on the possible use of nepheline syenite, originated as a mine byproduct, in alumina production through leaching with an azeotropic HCl solution. Previous work on nepheline syenite dissolution focused more on the extraction of potassium and sodium values. In this work, emphasis is given at the characteristics and leachability of aluminum content phases by applying a high temperature HCl leaching in untreated material. From this point of view, leaching experiments were conducted on nepheline syenite, at a temperature range of 90 °C to 150 °C and with aqueous azeotropic HCl solution. Leaching, in the aforementioned conditions, is a process, characterized by medium aluminum dissolution. The results show that the aluminum-bearing phases that withstand the dissolution process are mainly the ones of sodium and potassium feldspars.

Primary aluminum production is dependent on the Bayer process for Al₂O₃ refining and the Hall–Héroult process for Al production. Both these processes face serious sustainability challenges, while the overall Al supply chain is inflexible and prone to disruptions. One solution to the aforementioned challenges is the adoption of alternative Al₂O₃ production processes from a variety of primary and secondary raw materials. This research paper explores the potential use of bauxite tailings as an alternative secondary resource for alumina production, with an aqueous HCl process technology. Bauxite tailings are solid waste produced during the mining and beneficiation of certain bauxites before their digestion in the Bayer process. The research was conducted in two stages. Initially, 24 h trials using aqueous 5.9 M HCl solution and a 5:100 g/mL solid-to-liquid (S/L) ratio revealed complete dissolution of Al and near-complete dissolution of Fe. In the second stage, investigations involving higher S/L ratios under the same conditions confirmed that an S/L ratio of 20:100 g/mL represented the optimal parameters for bauxite tailings leaching, producing a 36.8 g/L Al and 25.2 g/L Fe concentration solutions. The PLS produced under the optimum conditions is suitable for downstream processing for the production of AlCl₃·6H₂O.

The extensive consumption of aluminum, combined with the shortage of the existing raw materials, and particularly bauxite, necessitates the exploitation of alternative raw materials for the production of alumina. The present paper focuses on the possible use of kaolin, as an abundant, cheap and high-aluminum content raw material, in alumina production, via the application of the Aranda-Mastin technology in the leaching step. From this point of view, leaching experiments were conducted on untreated kaolin and thermally treated, metakaolin, applying atmospheric pressure, temperature of 90 °C and with an aqueous solution of a low HCl concentration as the leaching agent. Leaching, in the aforementioned conditions, is an industrially applied process, characterized by highly efficient aluminum dissolution in the case of metakaolin with low silicon dissolution at a short retention time, but with respectively lower achieved results for untreated kaolin. In order to raise the aluminum dissolution rate from untreated material, temporal and subsequently chemical intensification was applied. The analysis indicated a higher aluminum dissolution rate, up to 70%, with the application of a high acid concentration of leaching agent, performed for a long retention time that could be further improved.