For the first time, deoxyribonucleic acid (DNA) from herring sperm has been employed as a novel flame retardant system for enhancing the thermal stability and flame retardant properties of cotton fabrics. Indeed, DNA could be considered an intrinsically intumescent flame retardant as it contains the three main components that are usually present in an intumescent formulation, namely: the phosphate groups, able to produce phosphoric acid, the deoxyribose units acting as a carbon source and blowing agents (upon heating a (poly)saccharide dehydrates forming char and releasing water) and the nitrogen-containing bases (guanine, adenine, thymine, and cytosine) that may release ammonia. The flammability tests in horizontal configuration have clearly shown that after two applications of a methane flame for 3 s, the DNA-treated cotton fabrics do not burn at all. Furthermore, when exposed to an irradiative heat flux of 35 kW m⁻², no ignition has been observed. Finally, an LOI value of 28% has been achieved for the treated fabrics as opposed to 18% of the untreated fabric.

This paper aims at updating the progress on the phosphorus-based flame retardants specifically designed and developed for fibers and fabrics (particularly referring to cotton, polyester and their blends) over the last five years. Indeed, as clearly depicted by Horrocks in a recent review, the world of flame retardants for textiles is still experiencing some changes that are focused on topics like the improvement of its effectiveness and the replacement of toxic chemical products with counterparts that have low environmental impact and, hence, are more sustainable. In this context, phosphorus-based compounds play a key role and may lead, possibly in combination with silicon- or nitrogen-containing structures, to the design of new, efficient flame retardants for fibers and fabrics. Therefore, this review thoroughly describes the advances and the potentialities offered by the phosphorus-based products recently developed at a lab-scale, highlighting the current limitations, open challenges and some perspectives toward their possible exploitation at a larger scale.

The synthesis and processing of most thermoplastics and thermoset polymeric materials rely on energy-inefficient and environmentally burdensome manufacturing methods. Frontal polymerization is an attractive, scalable alternative due to its exploitation of polymerization heat that is generally wasted and unutilized. The only external energy needed for frontal polymerization is an initial thermal (or photo) stimulus that locally ignites the reaction. The subsequent reaction exothermicity provides local heating; the transport of this thermal energy to neighboring monomers in either a liquid or gel-like state results in a self-perpetuating reaction zone that provides fully cured thermosets and thermoplastics. Propagation of this polymerization front continues through the unreacted monomer media until either all reactants are consumed or sufficient heat loss stalls further reaction. Several different polymerization mechanisms support frontal processes, including free-radical, cat- or anionic, amine-cure epoxides, and ring-opening metathesis polymerization. The choice of monomer, initiator/catalyst, and additives dictates how fast the polymer front traverses the reactant medium, as well as the maximum temperature achievable. Numerous applications of frontally generated materials exist, ranging from porous substrate reinforcement to fabrication of patterned composites. In this review, we examine in detail the physical and chemical phenomena that govern frontal polymerization, as well as outline the existing applications.

Polyurethanes (PUs) represent a family of useful synthetic polymers (thermoplastic or thermosetting) obtained from diisocyanates and diols/polyols via polycondensation reactions.