The contact angle is one of the most sensitive experimental values describing a junction between three phases, being influenced by the composition and properties of contacting media as well as the structure and composition of interfaces involved. The origins and importance of the contact angle in analysis of three-phase systems date back to the famous works on cohesion and adhesion of fluids published by Thomas Young in 1805 and later by Athanase Dupré in 1869. Since then, the contact angle has remained one of the most important values measured experimentally during characterization of solids and their wetting characteristics. Such measurements, however, involve solid surfaces that deviate from the idealized ones used in thermodynamic and mechanical modeling of three-phase junctions by Young, Dupré and others, and there is typically more than one value of contact angle measured on such surfaces. As a result, the attention of scientists and researchers in the past two centuries has been on development of methods for accurate contact angle measurements, interpretation of experimental values and understanding of the causes of contact angle value variation and contact angle hysteresis. This paper reviews advancements made in interpretation of experimental contact angles and their use in characterization of solid surfaces.

We report a new efficient method for fabricating a superhydrophobic oxidized surface of aluminum alloys with enhanced resistance to pitting corrosion in sodium chloride solutions. The developed coatings are considered very prospective materials for the automotive industry, shipbuilding, aviation, construction, and medicine. The method is based on nanosecond laser treatment of the surface followed by chemisorption of a hydrophobic agent to achieve the superhydrophobic state of the alloy surface. We have shown that the surface texturing used to fabricate multimodal roughness of the surface may be simultaneously used for modifying the physicochemical properties of the thick surface layer of the substrate itself. Electrochemical and wetting experiments demonstrated that the superhydrophobic state of the metal surface inhibits corrosion processes in chloride solutions for a few days. However, during long-term contact of a superhydrophobic coating with a solution, the wetted area of the coating is subjected to corrosion processes due to the formation of defects. In contrast, the combination of an oxide layer with good barrier properties and the superhydrophobic state of the coating provides remarkable corrosion resistance. The mechanisms for enhancing corrosion protective properties are discussed.