Polylactic acid (PLA) is produced from renewable materials, has a low melting temperature and has a low carbon footprint. These advantages have led to the extensive use of polylactic acid in additive manufacturing, particularly by fused filament fabrication (FFF). PLA parts that are 3D printed for industrial applications require stable mechanical properties and predictability regarding their dependence on the process parameters. Therefore, the development of the FFF process has been continuously accompanied by the development of software packages that generate CNC codes for the printers. A large number of user-controllable process parameters have been introduced in these software packages. In this respect, a lot of articles in the specialized literature address the issue of the influence of the process parameters on the mechanical properties of 3D-printed specimens. A systematic review of the research targeting the influence of process parameters on the mechanical properties of PLA specimens additively manufactured by fused filament fabrication was carried out by the authors of this paper. Six process parameters (layer thickness, printing speed, printing temperature, build plate temperature, build orientation and raster angle) were followed. The mechanical behavior was evaluated by tensile, compressive and bending properties.

Among the FDM process variables, one of the less addressed in previous research is the filament color. Moreover, if not explicitly targeted, the filament color is usually not even mentioned. Aiming to point out if, and to what extent, the color of the PLA filaments influences the dimensional precision and the mechanical strength of FDM prints, the authors of the present research carried out experiments on tensile specimens. The variable parameters were the layer height (0.05 mm, 0.10 mm, 0.15 mm, 0.20 mm) and the material color (natural, black, red, grey). The experimental results clearly showed that the filament color is an influential factor for the dimensional accuracy as well as for the tensile strength of the FDM printed PLA parts. Moreover, the two way ANOVA test performed revealed that the strongest effect on the tensile strength was exerted by the PLA color (η² = 97.3%), followed by the layer height (η² = 85.5%) and the interaction between the PLA color and the layer height (η² = 80.0%). Under the same printing conditions, the best dimensional accuracy was ensured by the black PLA (0.17% width deviations, respectively 5.48% height deviations), whilst the grey PLA showed the highest ultimate tensile strength values (between 57.10 MPa and 59.82 MPa).

The printing variable least addressed in previous research aiming to reveal the effect of the FFF process parameters on the printed PLA part’s quality and properties is the filament color. Moreover, the color of the PLA, as well as its manufacturer, are rarely mentioned when the experimental conditions for the printing of the samples are described, although current existing data reveal that their influence on the final characteristics of the print should not be neglected. In order to point out the importance of this influential parameter, a natural and a black-colored PLA filament, produced by the same manufacturer, were selected. The dimensional accuracy, tensile strength, and friction properties of the samples were analyzed and compared for printing temperatures ranging from 200 °C up to 240 °C. The experimental results clearly showed different characteristics depending on the polymer color of samples printed under the same conditions. Therefore, the optimization of the FFF process parameters for the 3D-printing of PLA should always start with the proper selection of the type of the PLA material, regarding both its color and the fabricant.

Additive manufacturing technologies enable the production of components with lightweight cores, by means of infills with various patterns and densities. Together with reduced mass and material consumption, infill geometries must ensure that strength and stiffness conditions are fulfilled. For the proper correlation of the infill type with the loading case of the part, the mechanical behavior of the infill along all three principal axes of inertia has to be known. In this paper, the behavior in symmetric and asymmetric bending of three infill geometries, commonly used in 3D printing processes (honeycomb, grid and triangles) is analyzed. The variations of deflections as a function of force orientation are presented, showing that honeycomb and triangular structures exhibit similar behaviors along the Y and Z principal axes of inertia. Furthermore, the displacements obtained for the three types of structures are compared, in relation to the consumed volume of material. The larger displacements of the grid structure compared to the honeycomb and triangular structures are highlighted.

Virtual instruments are used nowadays for measurement and control, but also as educational tools for students, being well accepted and stimulating innovation in the process of exploring the real world. It leads to discover interrelations, the phenomena are easier undersold and theory is better assimilated. The tool can be used in real laboratories as well as in virtual laboratories, constituting a support for self-learning or distance learning. This article presents how virtual instruments can be used in engineering education, with examples from our Vibration Laboratory, together with a qualitative research regarding the perception of students to this issue.