Nanofibrillated cellulose from eucalyptus pulp, produced by high-pressure homogenization, was used as cement partial replacement for cement paste at a content ranging from 0% to 0.5% by weight of cement. The effect of the content of nanofibrillated cellulose on porosity, thermal properties, compressive strength and degree of cement hydration was investigated. Results have shown an improvement in the compressive strength by more than 50% with 0.3 wt% of added nanofibrillated cellulose. The porosity was reduced by nanofibrillated cellulose addition, and the greatest result was achieved with mixture incorporating 0.3 wt% nanofibrillated cellulose. The coefficient of thermal expansion and the thermal conductivity measurements, relative to nanofibrillated cellulose-reinforced cement pastes, have pointed out the reinforcement effectiveness of nanofibrillated cellulose. The degree of cement hydration has increased with nanofibrillated cellulose content. This trend was confirmed by X-ray diffraction and Fourier Transform Infrared spectroscopy. These analyses have revealed that the presence of nanofibrillated cellulose promoted the hydration of cement, by producing more portlandite and calcium silicate gel, which is likely the main reason accounting for the strong enhancement in the compressive strength.

A nanostructured disordered Fe(Al) solid solution was obtained from elemental powders of Fe and Al using a high‐energy ball mill. The transformations occurring in the material during milling were studied with the use of X‐ray diffraction. In addition lattice microstrain, average crystallite size, dislocation density, and the lattice parameter were determined. Scanning electron microscopy (SEM) was employed to examine the morphology of the samples as a function of milling times. Thermal behaviour of the milled powders was examined by differential scanning calorimetry (DSC). The results, as well as dissimilarity between calorimetric curves of the powders after 2 and 20 h of milling, indicated the formation of a nanostructured Fe(Al) solid solution.