This study investigates the skid resistance performance of asphalt mixtures containing composite aggregates of basalt and limestone. The research aimed to predict the service life of the asphalt mixtures and identify the optimal basalt content for enhanced performance. Using an accelerated friction tester, friction indices such as the British pendulum number (BPN), mean texture depth (MTD), and dynamic friction coefficient (Dµ) were measured. The study conducted accelerated wear tests on mixtures with varying basalt contents under different water flow rates and loads. Results indicate that anti-skid performance decreased with increasing water flow, load, and wear cycles, initially showing a sharp decline followed by a gradual stabilization. Orthogonal experiments determined that basalt content had the most significant impact on skid resistance, followed by load and water flow rate. By converting skid resistance and MTD values into IFI values, a four-area diagram was created to illustrate skid resistance deterioration. The four-area IFI diagram also demonstrated that higher basalt content significantly enhances the skid resistance and service life of asphalt mixtures. Cost analysis based on life prediction showed that a 40% basalt content mixture is cost effective while maintaining excellent skid resistance. A test section study further validated that a 40% basalt content ensures good skid resistance, with indoor test predictions aligning closely with field data. Although the test section has been operational for only two years, ongoing monitoring will provide further insights into long-term skid resistance performance.

The air void system purposely introduced by an air-entraining admixture (AEA) is of great significance for the protection of concrete from freeze–thaw damage. Fly ash has been globally used in concrete, while the unburnt carbon in fly ash can adsorb AEA molecules and, thus, increase the AEA demand. Previous studies primarily focused on the air content of fresh fly ash concrete. This paper aimed to explore the stability and distribution of air voids in fly ash concrete at the fresh state. To achieve this goal, eleven different fresh fly ash concrete mixtures with an initial air content of 6 ± 1% were prepared in the laboratory. Samples were taken at various times within 75 min after initial mixing to investigate the air content and air void distribution in fly ash concrete at the fresh state using a super air meter (SAM). The results indicated that there was no significant correlation between loss on ignition (LOI) of fly ash and AEA demand to achieve the initial air content of 6 ± 1%. Class C fly ash concrete tended to have a better air content retention than Class F fly ash concrete. Compared with LOI, AEA demand had a stronger correlation with air content retention. Most of the fly ash concrete mixtures had a satisfactory air void system immediately after mixing, but the SAM number showed an increasing trend over time, suggesting the coarsening of the air void system with time.