Dynamic electrochemical impedance spectroscopy (dynamic EIS) has the capacity to track changes on surfaces in a changing corrosive system, an advantage it holds over classical EIS. We used the dynamic EIS approach to provide insight into the corrosion behavior of the AZ91D Mg alloy in simulated body fluid for 30 h at 25 °C. The results reveal that the impedance response of the alloy is influenced by the immersion time. Between 0 and 7 h, impedance with three time constants was obtained, whereas two-time-constant impedance spectra were obtained between 8 and 30 h of immersion. The results confirm the breakdown of the corrosion product at longer immersion times.

The efficacy of 1-butyl-1-methylpiperidinium tetrafluoroborate (BMPTFB) in retarding St37 steel corrosion in HCl environment has been examined using potentiodynamic polarization (PDP), electrochemical impedance spectroscopy (EIS), dynamic-EIS (DEIS), scanning electron microscope (SEM), and Fourier transform infrared spectroscopy (FTIR) techniques. Results from all applied methods reveal that BMPTFB is effective in suppressing St37 dissolution in the studied corrosive medium. Inhibition efficiency of 88% has been achieved by 4 mM BMPTFB. From DEIS results, BMPTFB is found to perform better as corrosion inhibitor at longer immersion time. The charge transfer resistance of the metal is raised in the presence of 4 mM BMPTFB from 378 to 744 Ω cm² at 1 h and further increased to 867 Ω cm² at 4 h. BMPTFB, according to PDP result behaves as mixed-type corrosion inhibitor. Corrosion inhibition by BMPTFB is via adsorption which can best be explained using El-Awady kinetic/thermodynamic adsorption isotherm. K_ads and values indicate that physisorption is the mechanism of adsorption of BMPTFB molecules onto St37 surface. The presence of BMPTFB molecules on St37 surface has been verified by SEM and FTIR.