Lignin (LIG) is a renewable biopolymer with well-known antimicrobial and antioxidant properties. In the present work LIG was combined with poly(butylene succinate) (PBS), a biocompatible/biodegradable polymer, to obtain composites with antimicrobial and antioxidant properties. Hot melt extrusion was used to prepare composites containing up to 15% (w/w) of LIG. Water contact angle measurements suggested that the incorporation of LIG did not alter the wettability of the material. The material density increased slightly when LIG was incorporated (<1%). Moreover, the melt flow index test showed an increase in the fluidity of the material (from 6.9 to 27.7 g/10 min) by increasing the LIG content. The Young's modulus and the tensile deformation of the material were practically unaffected when LIG was added. Infrared spectroscopy and differential scanning calorimeter confirmed that there were interactions between LIG and PBS. The DPPH assay was used to evaluate the antioxidant properties of the materials. The results suggested that all the materials were capable of reducing the DPPH concentrations up to 80% in <5 h. Finally, LIG-containing composites showed resistance to adherence of the common nosocomial pathogen, Staphylococcus aureus. All tested materials showed ca. 90% less bacterial adherence than PBS.

Cellulose nanofibers (CNF) are interesting biopolymers that find numerous applications in different scientific and technological fields. However, manufacturing costs are still one of the main drawbacks for the industrial production of highly fibrillated, transparent CNF suspensions. In the present study, cellulose nanofibers were produced from bleached eucalyptus pulp via TEMPO-mediated oxidation with varying amounts of NaClO and passed through a high-pressure homogenizer. The CNFs were chemically and physically characterized; cellulose nanopapers were also produced to study tensile properties. Production costs were also calculated. Results indicated that CNF properties are strongly dependent on the carboxyl content. Manufacturing costs showed that chemicals, in particular TEMPO catalyst, represent a large part of the final cost of CNFs. In order to solve this problem, a set of samples were prepared where the amount of TEMPO was gradually reduced. Characterization of samples prepared in this way showed that not only were the costs reduced, but also that the final properties of the CNFs were not significantly affected when the amount of TEMPO was reduced to half.