The growing interest in modern polymer materials has targeted research on complex plastic coatings and the possibilities of modifying their features and properties during manufacturing. Today’s modern coatings, including polyurea and polyurethane, are among the most modern developed resins. Compared to other polymer coatings, they are distinguished by their versatility, strength, and durability. They undoubtedly represent the next step in the evolution of coatings. Advances in coating technology have also led to the development of spray, injection, and roto-cast application equipment, improving polyurea-based elastomers’ performance. For many years, there has been much interest in increasing the flame resistance of polymers. This is dictated by safety considerations and the increasing requirements for the flammability of plastics, the area of application of which is growing every year. This text attempts to provide an overview of current research on flame retardant composites. Particular attention was paid to polyurea (PU) and polyurea-based hybrids and the application areas of polyurea coatings. The paper defines flame retardants, discusses how they work, and presents the types of flame retardants and the current trends of their usage in the production of plastics.

Polyurea is a synthetic material made by the reaction of isocyanate and polymer blend-containing amines. Due to its outstanding mechanical properties and fast curing, polyurea-based coatings have found dozens of applications, including waterproofing and anti-corrosion coatings. Further development of this material can create a flame-retardant product, a good alternative for common products available on the market, such as intumescent coatings. To improve the flame retardancy of polyurea, several flame retardants were investigated. The influence of aluminum hydroxide, resorcinol bis(diphenyl phosphate) (RDP), and tris chloropropyl phosphate (TCPP) on flame retardancy and morphology was studied. The following methods were used: infrared spectroscopy, scanning electron microscopy, thermogravimetric analysis, limiting oxygen index, and tensile strength. The examinations mentioned above showed the improvement of flame-retardancy of polyurea for two products: chlorinated organophosphate and organophosphate. Nevertheless, using the chlorinated organophosphate additive caused a rapid deterioration of mechanical properties.

The growing interest in modern polymer materials targeted the research on complex plastic coatings and the possibilities of modifying their features and properties during manufacturing. Today's modern coatings, including polyurea and polyurethane, are among the most modern developed resins. Compared to other polymer coatings, they are distinguished by their versatility, strength, and durability. They undoubtedly represent the next step in the evolution of coatings. Advances in coating technology have also led to the development of spray, injection, and roto-cast application equipment, improving polyurea-based elastomers’ performance. For many years, there has been much interest in increasing the flame resistance of polymers. This is dictated by safety considerations and the increasing requirements for the flammability of plastics, the area of application of which is growing every year. This text attempts to provide an overview of current research on flame retardant composites. Particular attention was paid to polyurea (PU) and polyurea-based hybrids and the application areas of polyurea coatings. The paper defines flame retardants, discusses how they work, and presents types of flame retardants and the current trends of their usage in the production of plastics.

This paper presents the results of tests on elastomer coatings based on polyurea–polyurethane formulation with increased fire parameters. Coatings modified with flame retardants: bis(phenylphosphate) resorcinol (RDP), trischloropropyl phosphate (TCPP), and aluminum hydroxide (ATH) were tested. Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA/DTG) were used to investigate the structure and thermal stability. The effectiveness of resorcinol bis(phenylphosphate) (RDP), tris chloropropyl phosphate (TCPP), and aluminum hydroxide (ATH) on heat release rate (HRR), smoke release rate (RSR), and oxygen consumption was evaluated using cone calorimetry. The cone calorimetry results were correlated with the mechanical properties of the coatings. The cone calorimetry analysis showed suitable organophosphorus flame retardant (FR) performance, significantly decreasing HRR and oxygen consumption. Additionally, 15% TCPP caused a reduction of HRR by over 50%, obtaining 211.4 kW/m² and pHRR by over 55%, reaching 538.3 kW/m². However, organophosphorus flame retardants caused a significant deterioration of mechanical properties simultaneously. Introducing a mixture of two FRs (RDP/TCPP) resulted in obtaining a coating with improved fire resistance and maintained good mechanical strength. The polyurea–polyurethane coating, modified with a mixture of two RDP/TCPP retardants (10:5), was simulated for the burning of roof systems. The result of the simulation was assessed positively. Thus, finally, it was confirmed that the proposed polyurea–polyurethane coating achieved the assumed flame retardant level.