The photocatalytic activity of silver-based catalysts containing different amounts of molybdenum disulfide (MoS₂; 5, 10 and 20 wt.%) was evaluated by the degradation of the antibiotic ciprofloxacin and the production of hydrogen via water splitting. All the silver (Ag)-based catalysts degraded more than 70% of the antibiotic in 60 min. The catalyst that exhibited the best result was 5%Ag@TiO₂-P25-5%MoS₂, with ca. 91% of degradation. The control experiments and stability tests showed that photocatalysis was the degradation pathway and the selected silver-based catalysts were stable after seven cycles, with less than 2% loss of efficiency per cycle and less than 7% after seven cycles. The catalyst with the highest hydrogen production was 5%Ag@TiO₂ NWs-20%MoS₂, 1792 μmol/hg, at a wavelength of 400 nm. This amount was ca. 32 times greater than that obtained by the pristine titanium oxide nanowires catalyst. The enhancement was attributed to the high surface area of the catalysts, along with the synergism created by the silver nanoparticles and MoS₂. All the catalysts were characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Raman spectroscopy, field-emission scanning electron microscopy (FE-SEM), high-resolution transmission electron microscopy (HRTEM), Brunauer–Emmett–Teller (BET) surface area analysis and energy dispersive X-ray spectroscopy (EDS).

For some decades, the scientific community has been looking for alternatives to the use of fossil fuels that allow for the planet’s sustainable and environmentally-friendly development. To do this, attempts have been made to mimic some processes that occur in nature, among which the photosystem-II stands out, which allows water splitting operating with different steps to generate oxygen and hydrogen. This research presents promising results using synthetic catalysts, which try to simulate some natural processes, and which are based on Au@ZnO–graphene compounds. These catalysts were prepared by incorporating different amounts of gold nanoparticles (1 wt.%, 3 wt.%, 5 wt.%, 10 wt.%) and graphene (1 wt.%) on the surface of synthesized zinc oxide nanowires (ZnO NWs), and zinc oxide nanoparticles (ZnO NPs), along with a commercial form (commercial ZnO) for comparison purposes. The highest amount of hydrogen (1127 μmol/hg) was reported by ZnO NWs with a gold and graphene loadings of 10 wt.% and 1 wt.%, respectively, under irradiation at 400 nm. Quantities of 759 μmol/hg and 709 μmol/hg were obtained with catalysts based on ZnO NPs and commercial ZnO, respectively. The photocatalytic activity of all composites increased with respect to the bare semiconductors, being 2.5 times higher in ZnO NWs, 8.8 times higher for ZnO NPs, and 7.5 times higher for commercial ZnO. The high photocatalytic activity of the catalysts is attributed, mainly, to the synergism between the different amount of gold and graphene incorporated, and the surface area of the composites.