Relaxor-lead titanate (PbTiO₃) crystals, which exhibit extremely high piezoelectricity, are believed to possess high electro-optic (EO) coefficients. However, the optical transparency of relaxor-PbTiO₃crystals is severely reduced as a result of light scattering and reflection by domain walls, limiting electro-optic applications. Through synergistic design of a ferroelectric phase, crystal orientation, and poling technique, we successfully removed all light-scattering domain walls and achieved an extremely high transmittance of 99.6% in antireflection film–coated crystals, with an ultrahigh EO coefficientr₃₃of 900 picometers per volt (pm V⁻¹), >30 times as high as that of conventionally used EO crystals. Using these crystals, we fabricated ultracompact EO Q-switches that require very low driving voltages, with superior performance to that of commercial Q-switches. Development of these materials is important for the portability and low driving voltage of EO devices.

Supplying wireless power is a challenging technical problem of great importance for implantable biomedical devices. Here, we introduce a novel implantable piezoelectric ultrasound energy–harvesting device based on Sm-doped Pb(Mg _1/3 Nb _2/3 )O ₃ -PbTiO ₃ (Sm-PMN-PT) single crystal. The output power density of this device can reach up to 1.1 W/cm ² in vitro, which is 18 times higher than the previous record (60 mW/cm ² ). After being implanted in the rat brain, under 1-MHz ultrasound with a safe intensity of 212 mW/cm ² , the as-developed device can produce an instantaneous effective output power of 280 μW, which can immediately activate the periaqueductal gray brain area. The rat electrophysiological experiments under anesthesia and behavioral experiments demonstrate that our wireless-powered device is well qualified for deep brain stimulation and analgesia applications. These encouraging results provide new insights into the development of implantable devices in the future.

Relaxor-PbTiO₃ crystals possess ultrahigh piezoelectricity when compared with state-of-the-art Pb(Zr,Ti)O₃ ceramics. Recently, even higher piezoelectricity is observed in alternating current electric-field-poled (AC-poled) crystals. This poling technique may benefit many piezoelectric materials and corresponding applications. The scaling effect is quite important for piezoelectric applications, since the operational frequency of devices is associated with the dimension of piezoelectric elements. Here, we investigated the thickness dependence of dielectric and piezoelectric properties for AC-poled relaxor-PbTiO₃ crystals. Compared with the traditional poling method, the piezoelectric coefficient (d₃₃) and dielectric permittivity (ɛ^T₃₃/ɛ₀) were found to be increased by 20%-30% via alternating current electric field poling (AC-poling). A weak scaling effect was observed for the samples with thickness above 200 μm. While, for 100-μm samples, the dielectric permittivity was only enhanced by 6%, and a clear degradation of properties was observed when the cycle of alternating current electric field is beyond three. These features are thought to be associated with the impacts of surface damages for thin samples. Of particular interest is that the coercive field was found to decrease during AC-poling, which should be considered for the design of piezoelectric devices. This work provides important information for AC-poled relaxor-PbTiO₃ crystals and will benefit the piezoelectric applications using these crystals.

A fully-sampled two-dimensional (2D) matrix array ultrasonic transducer is essential for fast and accurate three-dimensional (3D) volumetric ultrasound imaging. However, these arrays, usually consisting of thousands of elements, not only face challenges of poor performance and complex wiring due to high-density elements and small element sizes but also put high requirements for electronic systems. Current commercially available fully-sampled matrix arrays, dividing the aperture into four fixed sub-apertures to reduce system channels through multiplexing are widely used. However, the fixed sub-aperture configuration limits imaging flexibility and the gaps between sub-apertures lead to reduced imaging quality. In this study, we propose a high-performance multiplexed matrix array by the design of 1-3 piezocomposite and gapless sub-aperture configuration, as well as optimized matching layer materials. Furthermore, we introduce a sub-aperture volumetric imaging method based on the designed matrix array, enabling high-quality and flexible 3D ultrasound imaging with a low-cost 256-channel system. The influence of imaging parameters, including the number of sub-apertures and steering angle on imaging quality was investigated by simulation, in vitro, and in vivo imaging experiments. The fabricated matrix array has a center frequency of 3.4 MHz and a -6dB bandwidth above 70%. The proposed sub-aperture volumetric imaging method demonstrated a 10% improvement in spatial resolution, a 19% increase in signal-to-noise ratio, and a 57.7% increase in contrast-to-noise ratio compared with the fixed sub-aperture array imaging method. This study provides a new strategy for high-quality volumetric ultrasound imaging with a low-cost system.