Filamentous fungi colonize substrates by forming a mycelium. This network of hyphae can be used as a bio-based material. Here, we assessed the impact of environmental growth conditions and deletion of the hydrophobin gene sc3 on material properties of the mycelium of the mushroom forming fungus Schizophyllum commune. Thermogravimetric analysis showed that Δsc3 mycelium retained more water with increasing temperature when compared to the wild type. The Young’s modulus (E) of the mycelium ranged between 438 and 913 MPa when the wild type strain was grown in the dark or in the light at low or high CO₂ levels. This was accompanied by a maximum tensile strength (σ) of 5.1–9.6 MPa. In contrast, E and σ of the Δsc3 strain were 3–4- fold higher with values of 1237–2727 MPa and 15.6–40.4 MPa, respectively. These values correlated with mycelium density, while no differences in chemical composition of the mycelia were observed as shown by ATR-FTIR. Together, genetic modification and environmental growth conditions impact mechanical properties of the mycelium by affecting the density of the mycelium. As a result, mechanical properties of wild type mycelium were similar to those of natural materials, while those of Δsc3 were more similar to thermoplastics.

By embedding conductive yarns in, or onto, knitted textile fabrics, simple but robust stretch sensor garments can be manufactured. In that way resistance based sensors can be fully integrated in textiles without compromising wearing comfort, stretchiness, washability, and ease of use in daily life. The many studies on such textile strain sensors that have been published in recent years show that these sensors work in principle, but closer inspection reveals that many of them still have severe practical limitations like a too narrow working range, lack of sensitivity, and undesired time-dependent and hysteresis effects. For those that intend to use this technology it is difficult to determine which manufacturing parameters, shape, stitch type, and materials to apply to realize a functional sensor for a given application. This paper therefore aims to serve as a guideline for the fashion designers, electronic engineers, textile researchers, movement scientists, and human–computer interaction specialists planning to create stretch sensor garments. The paper is limited to textile based sensors that can be constructed using commercially available conductive yarns and existing knitting and embroidery equipment. Within this subtopic, relevant literature is discussed, and a detailed quantitative comparison is provided focusing on sensor characteristics like the gauge factor, working range, and hysteresis.