The effects of ex-situ annealing in a N2 ambient on the properties of GaAs/GaAsSbN/GaAs core-multi-shell nanowires on Si (111) substrate grown by self-catalyzed molecular beam epitaxy (MBE) are reported. As-grown nanowires exhibit band edge emission at ~0.99 eV with a shoulder peak at ~0.85 eV, identified to arise from band tail states. A large red shift of 7 cm−1 and broadened Raman spectra of as-grown nanowires compared to that of non-nitride nanowires confirmed phonon localization at N-induced localized defects. On annealing nanowires to 750 °C, there was no change in the planar defects in the nanowire with respect to the as-grown nanowire; however, vanishing of the photoluminescence (PL) peak corresponding to band tail states along with enhanced band edge PL intensity, recovery of the Raman shift and increase in the Schottky barrier height from 0.1 to 0.4 eV clearly point to the efficient annihilation of point defects in these GaAsSbN nanowires. A significant reduction in the temperature-induced energy shift in the annealed nanowires is attributed to annihilation of band tail states and weak temperature dependence of N-related localized states. The observation of room temperature PL signal in the 1.3 μm region shows that the strategy of adding small amounts of N to GaAsSb is a promising route to realization of efficient nanoscale light emitters with reduced temperature sensitivity in the telecommunication wavelength region.

Intrinsic and Te-doped GaAsSb nanowires with diameters ~100–120 nm were grown on a p-type Si(111) substrate by molecular beam epitaxy (MBE). Detailed magnetic, current/voltage and low-energy electron energy loss spectroscopy measurements were performed to investigate the effect of Te-doping. While intrinsic nanowires are diamagnetic over the temperature range 5–300 K, the Te-doped nanowires exhibit ferromagnetic behavior with the easy axis of magnetism perpendicular to the longitudinal axis of the nanowire. The temperature dependence of coercivity was analyzed and shown to be in agreement with a thermal activation model from 50–350 K but reveal more complex behavior in the low temperature regime. The EELS data show that Te doping introduced a high density of states (DOS) in the nanowire above the Fermi level in close proximity to the conduction band. The plausible origin of ferromagnetism in these Te-doped GaAsSb nanowires is discussed on the basis of d⁰ ferromagnetism, spin ordering of the Te dopants and the surface-state-induced magnetic ordering.

The importance of the heterojunction between the contact and cladding layers in the contact resistance of optoelectronic devices is investigated. The incorporation of a quaternary layer, intermediate in composition, between these layers is shown to provide specific contact resistances at least 60% lower with some $R_c$ values $<{10}^{-7}\Omega {\mathrm{cm}}^2$ and high-speed tandem modulators with an improved linearity and reduced series resistance. The lowering of the potential barrier for hole transport is most likely responsible for these observations. The thermal stability is quite good.