Waste electric and electronic equipment (WEEE) represents a potential secondary source of valuable materials, whose recovery is a growing business activity worldwide. In low-income countries, recycling is carried out under poorly controlled conditions resulting in severe environmental pollution. High concentrations of both metallic and organic pollutants have been confirmed in air, soil, water, and sediments in countries with informal recycling areas. The release of these contaminants into the environment presents a risk to the health of the exposed population that has been widely acknowledged but still needs to be quantified. The aim of this work was to evaluate the relative risk from inhalation associated with the open burning of different kinds of WEEE. The shrinking core model was applied to estimate the concentration of the metals which would be released into the environment during the incineration of different types of WEEE. In addition, the potential generation of dioxins during the same informal practice was estimated, based on the plastic content of the WEEE. The results provided for the first time a comparative analysis of the risk posed from the open burning of WEEE components, proposing a methodology to address the absolute risk assessment to workers from the informal recycling of WEEE.

Curcumin extracted from the rhizome of Curcuma Longa has been used in therapeutic preparations for centuries in different parts of the world. However, its bioactivity is limited by chemical instability, water insolubility, low bioavailability, and extensive metabolism. In this study, the coaxial electrospinning technique was used to produce both poly (ε-caprolactone) (PCL)–curcumin and core–shell nanofibers composed of PCL and curcumin in the core and poly (lactic acid) (PLA) in the shell. Morphology and physical properties, as well as the release of curcumin were studied and compared with neat PCL, showing the formation of randomly oriented, defect-free cylindrical fibers with a narrow distribution of the dimensions. The antibacterial and antibiofilm potential, including the capacity to interfere with the quorum-sensing mechanism, was evaluated on Pseudomonas aeruginosa PAO1, and Streptococcus mutans, two opportunistic pathogenic bacteria frequently associated with infections. The reported results demonstrated the ability of the Curcumin-loading membranes to inhibit both PAO1 and S. mutans biofilm growth and activity, thus representing a promising solution for the prevention of biofilm-associated infections. Moreover, the high biocompatibility and the ability to control the oxidative stress of damaged tissue, make the synthesized membranes useful as scaffolds in tissue engineering regeneration, helping to accelerate the healing process.

Bio-based membranes were obtained using Polyamide 11 (PA11) from renewable sources and a nano-hybrid composed of halloysite nanotubes (HNTs) filled with lysozyme (50 wt % of lysozyme), as a natural antimicrobial molecule. Composites were prepared using an electrospinning process, varying the nano-hybrid loading (i.e., 1.0, 2.5, 5.0 wt %). The morphology of the membranes was investigated through SEM analysis and there was found to be a narrow average fiber diameter (0.3–0.5 μm). The mechanical properties were analyzed and correlated to the nano-hybrid content. Controlled release of lysozyme was followed using UV spectrophotometry and the release kinetics were found to be dependent on HNTs–lysozyme loading. The experimental results were analyzed by a modified Gallagher–Corrigan model. The application of the produced membranes, as bio-based pads, for extending the shelf life of chicken slices has been tested and evaluated.

Water pollution is regarded as a dangerous problem that needs to be resolved right away. This is largely due to the positive correlation between the increase in global population and waste production, especially food waste. Hydrogel beads based on sodium alginate (Alg) and pomegranate fruit peels (PP) were developed for the adsorption of Safranin O dye (SO) in aqueous solutions. The obtained Alg−PP beads were widely characterized. The effects of the contact time (0–180 min), initial concentration (10–300 mg/L), initial pH (2–10), adsorbent dosage (1–40 g/L) and the temperature (293–333 K) were investigated through batch tests. The data proved that the adsorption kinetics of SO reached equilibrium within 30 min and up to 180 min. The dye adsorption is concentration dependent while a slight effect of pH was observed. The adsorption data of SO onto synthesized beads follow the pseudo second-order model. The experimental data fitted very well to Langmuir model with correlation factor of 0.92 which demonstrated the favourable nature of adsorption. The maximum adsorption capacity of Alg−PP could reach 30.769 mg/g at 293 K. Calculation of Gibbs free energy and enthalpy indicated that adsorption of SO onto Alg−PP is spontaneous (negative ΔG) and endothermic (ΔH = 9.30 kJ/mol). Analysis of diffusion and mass transport phenomena were presented. The removal efficiency was found to be 88% at the first cycle and decreased to 71% at the end of the seventh cycle. The reported results revealed that the Alg−PP beads could be used as a novel natural adsorbent for the removal of high concentrated solutions of Safranin O which is a cationic dye from liquid affluents and as future perspective, it can be used to remove various pollutants from wastewater.