Chemical Equilibrium Fracture Mechanics (CEFM) studies the effect of chemical reactions and phase transformations on crack-tip fields and material fracture toughness under chemical equilibrium. An important CEFM direction is hydrogen-induced embrittlement of alloys, due to several industrial applications, including those within the industrial value chain of hydrogen that is under development, which, according to European and international policies, are expected to contribute significantly to the replacement of fossil fuels by renewable energy sources. In the present study, the effect of hydrogen on the crack-tip fields of hydride- and non-hydride-forming alloys is examined. The crack-tip stress and hydrogen concentration distributions are derived under hydrogen chemical equilibrium, which is approached by considering the coupling of the operating physical mechanisms. In all cases, analytic relations are derived, thus facilitating integrity assessments, i.e., without the need to rely on complicated numerical methods, expected to lead to the development of respective tools in industrial applications. It is shown that, in the case of hydride precipitation, there are significant deviations from the K, HRR, and Prandtl fields, and, thus, the well-known approaches of Linear Elastic Fracture Mechanics (LEFM) and Elastic–Plastic Fracture Mechanics (EPFM) need to be accordingly modified/extended.

Hydrogen-induced crack growth initiation, in metallic structures, is studied under constant tem-perature and chemical equilibrium, by employing Chemical Equilibrium Fracture Mechanics (CEFM). The conditions of small-scale, contained and large-scale hydrogen embrittlement are in-troduced and the areas of material deterioration, together with the distributions of stresses and hydrogen concentration, including hydride volume fraction, are derived analytically. It is shown that the shape of the material deterioration zone is identical for embrittlement caused either by hydrogen in solid solution or by hydride precipitation; the size depends on the strength of the asymptotic crack-tip field, which develops by the mechanical loading in the hydrogen-free struc-ture, as well as on the average hydrogen content absorbed by the structure. It is also shown that a linear relation exists between a power of the threshold of crack-growth initiation and the logarithm of hydrogen content, depending on the extent of hydrogen embrittlement and material elastic-plastic deformation. The predictions of the present analysis are confirmed by published experimental fracture mechanics measurements on several non-hydride and hydride forming alloys, including α/β hydride forming alloys. The present study facilitates structural integrity assessments, significantly, without relying on complicated coupled numerical analysis of material deformation, hydrogen diffusion and hydride precipitation.