Novel silver nanoparticles from Gleichenia Pectinata (Willd.) C. Presl. was synthesized. A combination of spectroscopic and microscopic techniques were utilized to characterize the newly synthesized Gleichenia Pectinata Silver Nanoparticles (GPAgNPs) vis-à-vis UV-Vis Spectroscopy, Fourier Transform Infra-Red (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), Energy Dispersive X-ray Spectroscopy (EDX) and X-Ray Diffraction (XRD) Analyses. Significant absorption was observed at 460 nm resulting from the surface Plasmon resonance (SPR). A rapid rate of synthesis was observed and the best surface plasmon resonance was obtained at 105 minutes contact time. SEM and TEM showed an spherical shape of GPAgNPs with an average size of 7.51 nm. The XRD result revealed a crystalline and polydispersed GPAgNPs. GPAgNPs were effective against four antibiotic resistant pathogens and they exhibited excellent antimicrobial activity against Pseudomonas aeruginosa, Escherichia coli, Klebsiella pneumoniae and Candida albicans. GPAgNPs favorably competed with standard antibiotics. This therefore enlisted GPAgNPs as potential antimicrobial and therapeutic agents against multidrug resistant micro-organisms (MDRM).

Adsorption of problematic copper ions as one of the endocrine disruptive substances from aqueous solution onto nanoscale zerovalent iron (nZVI) was studied. The high pore size 186.9268 Å, pore diameter 240.753 Å, and BET surface area 20.8643 m² g⁻¹ and pH(pzc) enlisted nZVI as an efficient nano-adsorbent for treatment of heavy metals from synthetic wastewater. SEM and EDX revealed the morphology and elemental distribution before and after adsorption. 98.31% removal efficiency was achieved at optimum adsorption operational parameters. Of all the thirteen isotherm models, equilibrium data were well fitted to Langmuir. Kinetics and mechanism data across the concentrations from 10 to 200 mg L⁻¹ were analyzed by ten models. PSO best described kinetics data as confirmed by various statistical error validity models. The intraparticle diffusion model described that the intraparticle diffusion was not the only rate-limiting step. The adsorption mechanism was diffusion governed established by Bangham and Boyd models. Feasible, spontaneous, endothermic, and degree of randomness were reveal by the thermodynamic studies. Better desorption index and efficiency were obtained using HCl suggesting multiple mechanism processes. The performance of ZVI suggested it has a great potential for effective removal of endocrine disruptive cationic contaminant from wastewater.

Background: There is a growing interest in the green synthesis of silver nanoparticles (AgNPs) using plant extract because the technique is cost effective, eco-friendly and environmentally benign. This is phasing out the use of toxic and hazardous chemical earlier reported. Tithonia diversifolia is a wild sunflower that grows widely in the western part of Nigeria with a proven medicinal benefit. However, several studies carried out have left doubts on the basic operational parameters needed for the green synthesis of AgNPs. The objective of this work was to carry out green synthesis of AgNPs using T. diversifolia extract via an eco-friendly route through optimization of various operational parameters, characterization, and antimicrobial studies. Method: Green synthesis of TD-AgNPs was done via bottom-up approach through wet chemistry technique using environmentally benign T. diversifolia plant extract as both reducing and stabilizing agent. Phytochemical Screening of the TD plant extract was carried out. Experimental optimization of various operational parameters—reaction time, concentration, volume ratio, and temperature was investigated. TD-AgNPs were characterized by UV–Vis spectroscopy, FTIR Spectroscopy, SEM/energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), and transmission electron microscopy (TEM). Antimicrobial studies against multi drug resistant microorganisms (MDRM) were studied using the agar well diffusion method. Results: This study reveals the importance of various operational parameters in the synthesis of TD-AgNPs. Excellent surface plasmon resonance peaks (SPR) were obtained at optimum experimental factors of 90 min reaction time under room temperature at 0.001M concentration with the volume ratio of 1:9 (TD extract:Ag ion solution). The synthesis was monitored using UV–Vis and maximum wavelength obtained at 430 nm was due to SPR. The morphology and elemental constituents obtained by TEM, SEM, and EDX results revealed a spherical shape of AgNPs with prominent peak of Ag at 3.0 kV in EDX spectrum. The crystallinity nature was confirmed by XRD studies. FTIR analysis proved presence of biomolecules functioning as reducing, stabilizing, and capping agents. These biomolecules were confirmed to be flavonoid, triterpenes, and saponin from phytochemical screening. The antimicrobial studies of TD-AgNPs were tested against MDRM—Escherichia coli, Salmonella typhi, Salmonella enterica, and Bacillus subtilis. Discussion: The variation of reaction time, temperature, concentration, and volume ratio played substantive and fundamental roles in the synthesis of TD-AgNPs. A good dispersion of small spherical size between 10 and 26 nm was confirmed by TEM and SEM. A dual action mechanism of anti-microbial effects was provided by TD-AgNPs which are bactericidal and membrane-disruption. Based on the antimicrobial activity, the synthesized TD-AgNPs could find good application in medicine, pharmaceutical, biotechnology, and food science.

The stress on our water environment as a result of increased industrialization, which aids urbanization, is becoming very high thus reducing the availability of clean water. Polluted water is of great concern to the aquatic organism, plants, humans, and climate and indeed alters the ecosystem. The preservation of our water environment, which is embedded in sustainable development, must be well driven by all sectors. While effective wastewater treatment has the tendency of salvaging the water environment, integration of environmental policies into the actor firms core objectives coupled with continuous periodical enlightenment on the present and future consequences of environmental/water pollution will greatly assist in conserving the water environment.

Synthesis of nanoscale zerovalent manganese (nZVMn) by chemical reduction was carried out in a single pot system under inert environment. nZVMn was characterized using a combination of analytical techniques: Ultraviolet–Visible Spectroscopy, Fourier Transform Infrared Spectroscopy, Scanning Electron Microscopy, Transmission Electron Microscopy, Energy Dispersive X-ray, BET surface area and Point of Zero Charge. The adsorption physicochemical factors: pH, contact time, adsorbent dose, agitation speed, initial copper ion concentration and temperature were optimized. The kinetic data fitted better to Pseudo second-order, Elovich, fractional power and intraparticle diffusion models and their validity was tested by three statistical models: sum of square error, Chi-square (χ ²) and normalized standard deviation (Δq). Seven of the two-parameter isotherm models [Freundlich, Langmuir, Temkin, Dubinin–Kaganer–Raduskevich (DKR), Halsey, Harkin–Jura and Flory–Huggins] were used to analyse the equilibrium adsorption data. The Langmuir monolayer adsorption capacity (Q _max = 181.818 mg/g) obtained is greater than other those of nano-adsorbents utilized in adsorption of copper ions. The equilibrium adsorption data were better described by Langmuir, Freundlich, Temkin, DKR and Halsey isotherm models considering their coefficient of regression (R ² > 0.90). The values of the thermodynamic parameters: standard enthalpy change ∆H° (+50.27848 kJ mol⁻¹), standard entropy change ∆S° (203.5724 J mol⁻¹ K⁻¹) and the Gibbs free energy change ∆G° revealed that the adsorption process was feasible, spontaneous, and endothermic in nature. The performance of this novel nanoscale zerovalent manganese (nZVMn) suggested that it has a great potential for effective removal of copper ions from aqueous solution.