The effects of three main factors, including polypropylene fiber content, composite cement content and curing time on the unconfined compressive strength of fiber-reinforced cemented clay were studied through a series of unconfined compressive strength tests. The experimental results show that the incorporation of fibers can increase the compressive strength and residual strength of cement-reinforced clay as well as the corresponding axial strain when the stress peak is reached compared with cement-reinforced clay. The compressive strength of fiber-reinforced cement clay decreases first, then increases with small-composite cement at curing time 14 d and 28 d. However, fiber-reinforced cement clay’s strength increases with the increase of fiber content for heavy-composite cement. The compressive strength of fiber-composite cement-reinforced marine clay increases with the increase of curing time and composite cement content. The growth rate increases with the increase of curing time. The failure mode of composite cement-reinforced clay is brittle failure, while the failure mode of fiber-reinforced cemented clay is plastic failure.

Backfilling mining method is an overlying strata control way, which is widely used in underground coal mine. This method is effective in preventing and controlling geological disasters such as surface subsidence, mine water inrush, rock burst, and other disasters. Cement-treated marine clay (CMC) is a typical porous media, which has abundant reserves and can be used as a new backfilling material. Therefore, the mechanical characteristics of CMC are very important for overlying strata control in coal mine. To investigate stress-strain behavior of CMC, isotropic consolidated drained (CID) triaxial test and isotropic compression test (ICT) were conducted with different confining pressures in the range of 50–800 kPa. Stress-strain behavior was found similar to those of the overconsolidated stress-strain behavior as well as the pore water pressure versus strain. Stress versus strain curves under lower confining pressure 50–250 kPa presented shear dilatancy. The result shows that the peak strength increased linearly with increasing confining pressure. The internal friction angle and cohesion are 48° and 590 kPa, respectively. Before the confining pressure reaches 727 kPa, which is the primary yielding point, the secant modulus E₁ (the secant modulus at 1% axial strain) and the secant modulus E₅₀ (corresponding to the 50% of the peak point) increase initially and decrease afterwards with the increasing of confining pressure. Afterwards, the two parameters increased with increasing confining pressure. The yielding stress occurred in the stage, generating a dramatic decrease in tangent modulus. This study can be a theoretical basis for engineering application of this new backfilling material.

This study deals with the variation in strength of clays stabilized by a special binder—the CEM II/B‐V type of Portland‐fly ash cement. Two sources of uncertainties were examined, that is, the uncertainty in cement fraction in the binder, and the nonuniformity in binder concentration resulted from the process of mixing binder slurry with in situ clays. These two uncertainties were quantitatively described as two random variables, and the analyses were conducted through the Monte Carlo simulation method. Results indicate that the strength is insensitive to the cement fraction in the binder but is sensitive to the binder concentration; the variation of the latter even results in an amplified variation of strength. The variation of binder concentration is proposed to be linked up with the variation of strength through the operational parameter of blade rotation number. By doing so, the results could benefit designers in quality control prior to the construction of soil stabilization.