Interlayer bond strength is one of the key aspects of 3D concrete printing. It is a well-established fact that, similar to other 3D printing process material designs, process parameters and printing environment can significantly affect the bond strength between layers of 3D printed concrete. The first section of this review paper highlights the importance of bond strength, which can affect the mechanical and durability properties of 3D printed structures. The next section summarizes all the testing and bond strength measurement methods adopted in the literature, including mechanical and microstructure characterization. Finally, the last two sections focus on the influence of critical parameters on bond strength and different strategies employed in the literature for improving the strength via strengthening mechanical interlocking in the layers and tailoring surface as well as interface reactions. This concise review work will provide a holistic perspective on the current state of the art of interlayer bond strength in 3D concrete printing process.

Cement production is environmentally unsustainable due to the high anthropogenic carbon emissions produced. Supplementary cementitious materials (SCMs), derived from the by-products of different industries, have been deemed an effective way to reduce carbon emissions. The reduction in carbon emissions is achieved by lowering the clinker factor of cement, through a partial replacement with an SCM. Sugarcane Bagasse Ash (SCBA) is produced as an agricultural waste from the sugarcane industry and has gained a lot of attention for being a feasible and readily available pozzolanic material, underutilised as an SCM. This study evaluates alkali-activated sugarcane bagasse ash’s mechanical and durability performance, at varied contents, in binary blended cement concrete and ternary blended cement concrete containing silica fume (SF). Potassium Hydroxide (KOH), used as the alkali activator, is intended to enhance the reactivity of the ash, with the possibility of a high-volume SCBA content. The mechanical performance was investigated by compressive and split tensile strength tests, and durability performance was investigated using the Oxygen Permeability Index (OPI) test. In addition, a micro-CT porosity test was conducted to assess how the microstructure and porosity of the concrete affect the mechanical and durability performance. The results indicated that using SCBA in a ternary blend with SF can significantly improve the overall performance and create less porous concrete. At 30% SCBA and 10% SF replacement, the performance tests revealed the highest mechanical strength and the lowest permeability, outperforming the control concrete and the binary blended cement concrete containing only SCBA.