Polycaprolactone (PCL) scaffolds have been widely investigated for tissue engineering applications, however, they exhibit poor cell adhesion and mechanical properties. Subsequently, PCL composites have been produced to improve the material properties. This study utilises a natural material, Bombyx mori silk microparticles (SMP) prepared by milling silk fibre, to produce a composite to enhance the scaffolds properties. Silk is biocompatible and biodegradable with excellent mechanical properties. However, there are no studies using SMPs as a reinforcing agent in a 3D printed thermoplastic polymer scaffold. PCL/SMP (10, 20, 30 wt%) composites were prepared by melt blending. Rheological analysis showed that SMP loading increased the shear thinning and storage modulus of the material. Scaffolds were fabricated using a screw-assisted extrusion-based additive manufacturing system. Scanning electron microscopy and X-ray microtomography was used to determine scaffold morphology. The scaffolds had high interconnectivity with regular printed fibres and pore morphologies within the designed parameters. Compressive mechanical testing showed that the addition of SMP significantly improved the compressive Young's modulus of the scaffolds. The scaffolds were more hydrophobic with the inclusion of SMP which was linked to a decrease in total protein adsorption. Cell behaviour was assessed using human adipose derived mesenchymal stem cells. A cytotoxic effect was observed at higher particle loading (30 wt%) after 7 days of culture. By day 21, 10 wt% loading showed significantly higher cell metabolic activity and proliferation, high cell viability, and cell migration throughout the scaffold. Calcium mineral deposition was observed on the scaffolds during cell culture. Large calcium mineral deposits were observed at 30 wt% and smaller calcium deposits were observed at 10 wt%. This study demonstrates that SMPs incorporated into a PCL scaffold provided effective mechanical reinforcement, improved the rate of degradation, and increased cell proliferation, demonstrating potential suitability for bone tissue engineering applications.

Recently, the development of sustainable and environmentally friendly biomaterials has gained the attention of researchers as potential alternatives to petroleum-based materials. Biomaterials are a promising candidate to mitigate sustainability issues due to their renewability, biodegradability, and cost-effectiveness. Thus, the purpose of this study is to explore a cost-effective biomaterial-based delivery system for delivering fertilizers to plants. To achieve this, rice straw (agro-waste) was selected as a raw material for the extraction of cellulose. The cellulose was extracted through alkali treatment (12% NaOH), followed by TEMPO-based oxidation. The cellulose nanofibers were characterized using Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy, and transmission electron microscopy. In scanning electron microscopy, a loosening of the fibrillar structure in cellulose nanofibers (CNFs) was observed with a diameter of 17 ± 4 nm. The CNFs were loaded with nitrogen-based fertilizer (ammonium chloride) in 1:1, 1:2, and 2:1 (w/w) proportions. The loading was estimated through surface charge variation; in the case of the 1:1 sample, maximum reductions in surface charge were seen from −42.0 mV to −12.8 mV due to the binding of positive ammonium ions. In the release kinetics study, a controlled release pattern was observed at 1:1, which showed a 58% cumulative release of ammonium ions within 8 days. Thus, the study paves the way for value-added uses of rice straw as an alternative to the current environmentally harmful practices.

The degumming process to remove sericin decreases silk fiber strength; however, the impact of degumming on the mechanical properties of regenerated silk biomaterials has not been established. This study investigated the effect of degumming temperature, time, alkaline component and alkaline concentration on the mechanical properties of silk fibroin films. Sericin removal was estimated using weight loss; 10 samples with 12.2–29.4% weight loss were then further characterized in terms of fiber mechanical properties, fiber surface morphology, molecular weight distribution and film tensile strength. A negative correlation was found between weight loss and fiber tensile strength. This loss of fiber strength under harsher degumming conditions had a direct impact on the tensile strength of regenerated films. Mild degumming conditions (weight loss of 12.2%) led to higher film strength (8.9 MPa), whereas aggressive degumming conditions (with 29.4% weight loss) resulted in significantly weaker films (4.3 MPa). The presence of some residual sericin, after mild degumming, is likely to affect the mechanical properties of the regenerated silk films. These results will assist in the development of materials with mechanical and biocompatibility properties tuned to specific biomedical applications.