The results of investigation on the oxidation behavior of orthorhombic Ti₂AlNb alloy are presented. Oxidation was carried out in static air atmosphere at two temperatures: 700 and 800 °C. The investigation of the material structure of the specimen and chemical composition of oxidation products was performed. It was determined that the alloy shows a sufficient high-temperature corrosion resistance only at 700 °C.

This paper presents research results on the oxidation of γ-TiAl-based alloys collected over many years. The oxidation exposures were carried out in air at 875–975 °C. Micro-areas close to the interface of the oxidation product–metallic substrate were analyzed. It was shown that the oxidation process takes place as a result of the outward diffusion of titanium ions, aluminum and alloying elements as well as the inward diffusion of oxygen and nitrogen, and the course of oxidation was also determined by the processes occurring in the metallic substrate.