Bead foams serve in a wide variety of applications, from insulation and packaging to midsoles in shoes. However, the currently used materials are limited to somewhat low temperature or exhibit significant changes in modulus in the temperature range of many applications due to their glass transition. By comparison, polycarbonate (PC) exhibits almost constant mechanics for temperatures up to 130 °C. Therefore, it appears as an advantageous base material for bead foams. The aim of the publication is to provide comprehensive data on the properties of expanded PC (EPC) in comparison to already commercially available expanded polypropylene, EPP, and expanded polyethylene-terephthalate, EPET. A special focus is set on the thermo-mechanical properties as these are the most lacking features in current materials. In this frame, dynamic mechanical analysis, and tensile, bending, compression and impact tests at room temperature (RT), 80 °C, and 110 °C are conducted for the three materials of the same density. Already at RT, EPC exhibits superior mechanics compared to its peers, which becomes more pronounced toward higher temperature. This comes from the low sensitivity of properties to temperature as EPC is used below its glass transition. In summary, EPC proves to be an outstanding foam material over a broad range of temperatures for structural applications.

Polypropylene (PP) is an outstanding material for polymeric foams due to its favorable mechanical and chemical properties. However, its low melt strength and fast crystallization result in unfavorable foaming properties. Long-chain branching of PP is regarded as a game changer in foaming due to the introduction of strain hardening, which stabilizes the foam morphology. In this work, a thorough characterization with respect to rheology and crystallization characteristics of a linear PP, a PP/PE-block co-polymer, and a long-chain branched PP are conducted. Using these results, the processing window in foam-extrusion trials with CO₂ and finally the foam properties are explained. Although only LCB-PP exhibits strain hardening, it neither provide the broadest foaming window nor the best foam quality. Therefore, multiwave experiments were conducted to study the gelation due to crystallization and its influence on foaming. Here, linear PP exhibited a gel-like behavior over a broad time frame, whereas the other two froze quickly. Thus, apart from strain hardening, the crystallization behavior/crystallization kinetics is of utmost importance for foaming in terms of a broad processing window, low-density, and good morphology. Therefore, the question arises, whether strain hardening is really essential for low density foams with a good cellular morphology.