Friction stir processing (FSP) has emerged as a valuable technique in the surface metal matrix composite fabrication field. In this process, solid-state processing mostly avoids the formation of detrimental phases inside composites. Despite having a high specific strength, further extensive Al alloy applications are limited due to their poor surface properties. A hybrid reinforcement approach can be used to improve surface properties. In this study, industrial waste fly ash material is mixed with hard SiC ceramic particles. The main focus of this research is to improve wear resistance under dry sliding conditions and microhardness of aluminum 7075-T651 by dispersion of silicon carbide-fly ash (SiC/fly ash) powder in a base alloy by FSP. The parameters used for this investigation are: tool rotation rpm (500, 1000 and 1500), the tool traverse mm/min (20, 30 and 40), the reinforcement’s hybrid ratio HR (60:40, 75:25 and 90:10) and the volume percentage vol.% (4%, 8% and 12%). The influence of these parameters on the resultant composite’s microstructure, dry sliding wear rate and micro-hardness was studied. By using response surface methodology (RSM), desirable ranges of process parameters for lower wear rate and higher microhardness were obtained. The interaction effect of SiC/fly ash volume percentage and hybrid ratio had the most influential effect on the wear rates, as well as microhardness of composites. Moreover, microhardness increased with an increase in the volume percentage of SiC/fly ash powders towards high SiC content in hybrid ratio. Interestingly, among stirring parameters, tool traverse speed was found to be more influential than tool rotational speed. The minimum wear rate was observed for the Run 20 sample (w: 1000 rpm, v: 40 mm/min, HR: 75:25, vol.%: 8). A maximum microhardness of 241.20 HV was achieved for Run 15 (w: 500 rpm, v: 40 mm/min, HR: 90:10, vol.%: 12) sample. Mainly, reinforcement distribution—in accordance with the stirring action generated by the tool—had a major role in controlling the surface properties of the resultant composites.

Friction stir processing (FSP) has evolved as an important technique in fabrication of metal matrix composites. The surface properties enhancement is obtainable by insertion of desired discontinuous particular reinforcements into base alloy using FSP. Despite having high specific strength, more applications of Al alloys are restricted due to their poor surface properties under various loading conditions. In this study, the main focus is on enhancing the microhardness and wear properties of Al 7075 base alloy by means of uniform dispersion of silicon carbide and graphite (SiC/Gr) nano particles into the base alloy using the FSP technique. The tool rotational speed (w: 500, 1000, 1500 rpm), tool traverse speed (v: 20, 30, 40 mm/min), reinforcement particles hybrid ratio (HR: 60:40, 75:25, 90:10) and volume percentage (vol%: 4%, 8%, 12%) are used as independent parameters. The effect of these parameters on microstructure, micro hardness and wear properties of surface composites are studied in detail. For desired wear rate and microhardness as responses, the aforementioned independent parameters are optimized using response surface methodology (RSM). The significance of factors and their interactions for maximizing hardness and minimizing wear rate and coefficient of friction (COF) were determined. Analysis of variance (ANOVA) for responses has been carried out, and the models were found to be significant in all three responses. The minimum wear rate of 0.01194 mg/m was obtained for parameters w 1500 rpm, v 40 mm/min, HR 60:40, vol% 4 (Run 10). The maximum micro hardness of 300 HV obtained for parameters w 1000 rpm, v 30 mm/min, HR 75:25, vol% 12 (Run 14). The presence and uniform distribution of SiC and Gr into the base alloy was confirmed through field-emission scanning electron microscopy (FESEM) imaging, energy-dispersive X-ray spectroscopy (EDX) and mapping tests. The wear rate and COF decreased significantly due to graphitized mechanically mixed layer developed at the sliding contacts. The microhardness of resultant composites observed to be dependent on effect of the independent parameters on extent of inherent precipitates dissolution and grain size strengthening in the resultant materials.

Polymeric materials such as High density polyethylene(HDPE) are ductile in nature, having very low strength. In order to improve strength by non-treated rigid fillers, polymeric materials become extremely brittle. Therefore, this work focuses on achieving pseudo-ductility (high strength and ductility) by using a combination of rigid filler particles (CaCO₃ and bentonite) instead of a single non-treated rigid filler particle. The results of all tensile-tested (D638 type i) samples signify that the microstructural features and surface properties of rigid nano fillers can render the required pseudo-ductility. The maximum value of tensile strength achieved is 120% of the virgin HDPE, and the value of elongation is retained by 100%. Furthermore, the morphological and fractographic analysis revealed that surfactants are not always going to obtain polymer–filler bonding, but the synergistic effect of filler particles can carry out sufficient bonding for stress transfer. Moreover, pseudo-ductility was achieved by a combination of rigid fillers (bentonite and CaCO₃) when the content of bentonite dominated as compared to CaCO₃. Thus, the achievement of pseudo-ductility by the synergistic effect of rigid particles is the significance of this study. Secondly, this combination of filler particles acted as an alternative for the application of surfactant and compatibilizer so that adverse effect on mechanical properties can be avoided.

In this report, naturally available materials have been utilized in the development of acoustic absorbers. This work presents the study of the effect of oil palm trunks dust (OPTD) loading to the mechanical and acoustical properties of elastomeric thermoplastic polyurethane (TPU). Four composite sheets of 3-mm thickness were prepared by varying the OPTD loadings with 10–40% wt into the polyurethane. Density, modulus elasticity, sound absorption coefficient and sound transmission loss of the samples were measured according to corresponding standards. The OPTD is found to reduce the density of the elastomeric polyurethane and at the same time, it increases the Young's modulus up to 215 MPa. The composite material can be applied as sound absorber panel installed in front of a rigid wall with an air gap. Increasing the air gap, thus lowering the air stiffness, shifts the absorption peak to a lower frequency. With OPTD loadings, the formation of micro-pores in the inner structure helps to improve the peak of sound absorption of the panel at the resonant frequency which can reach above 0.9. As the OPTD loading has effect on density, the effect on the sound transmission loss at the mass-controlled region is also apparent.