To improve the adsorption and separation efficiency of lead-containing wastewater by graphene oxide (GO), attapulgite (ATP) was used through a simple hydrothermal reaction. The prepared GO was characterized by SEM, TEM, FTIR, and XPS. The adsorption properties of the prepared GO were investigated. The maximum adsorption capacity of Pb²⁺ on as-prepared GO at pH 5 and 25 °C was 450.9 mg/g. It is concluded that the as-prepared GO can be used as a high-efficiency adsorbent for lead-containing wastewater.

This study investigated the ultrasonic–thermal regeneration of powdered activated carbon (PAC) spent using 4-chlorophenol (4-CP). Similarly, a thermal regeneration process was also studied and the reaction conditions (i.e., regeneration temperature, heating rate, regeneration time) were tested. Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) analysis were applied to characterize the regenerated PACs under different treatments (thermal, ultrasonic and ultrasonic–thermal) and also compare them with the fresh and exhausted PACs. According to our regeneration observations, the ideal regeneration parameters were determined to be a 40 kHz frequency, 0.18 W/mL sonication power, 0.1 M NaOH and 50% (v/v) ethyl alcohol as the regeneration solution, and 1 g/L of saturated PAC mass with thermal regeneration as the second stage at 500 °C, desorbed for 30 min with a heating rate of 20 °C min⁻¹. Under these conditions, the RE value achieved 90.99% and the η value reached 5.6%. The results of FTIR, XPS and XRD revealed that the oxygen functional group content of ultrasonic–thermal regenerated PAC significantly increased. These oxygenous groups exerted a positive effect on the adsorption process of the regenerated PAC and the subsequent adsorption–regeneration process.

For continuous and efficient oil/water separation and adsorption of dyes, coconut shell powder was grafted onto the surface of quartz sand by dip-coating method to make coconut shell powder-covered quartz sand filter media (CSQS) with superhydrophilic and underwater superoleophobic properties and superoleophilic and underoil highly hydrophobic properties. The contact angles of the underwater oil and underoil water with CSQS were more than 151.2° and 134.2°, respectively. A continuous oil/water separation device was designed. The separation device filled with CSQS can separate oil/water mixture (whether heavy or light oil) into water and oil at the same time with a separation efficiency of above 99.92%. The filter layer can be recovered through reverse extrusion even after lyophobic liquid penetrated the filter layer; hence, the separation efficiency of the filter layer was still above 99.99% for diesel and water mixture. Simultaneously, CSQS can effectively adsorb methylene blue with the highest removal rate as 98.94%. CSQS can maintain stable wettability under harsh environment conditions. This paper provides a new idea on continuous and efficient oil/water separation and simultaneous dye adsorption.

This paper aims to establish a more standardized and regulated carbon emission accounting model for sponge cities by unifying the accounting content for carbon emissions and clarifying the relationships between carbon reduction benefits, carbon reduction effects, and carbon sequestration, in order to evaluate the carbon reduction outcomes and mechanisms of sponge city construction. Based on a Life Cycle Assessment (LCA) carbon emission accounting model using the carbon emission factor method, a newly constructed residential area in Tianshui City, Gansu Province, was selected as a case study, and the carbon emission reduction effect of sponge city construction was then investigated. Results indicated that the 30-year full life cycle carbon emissions for sponge city construction in the newly constructed residential area amounted to 828.98 tons, compared to 744.28 tons of CO₂ reduction in traditional construction, representing a 47.31% reduction in carbon emissions. Over a 30-year life cycle, this equated to a total carbon emission reduction effect of 1460.31 tons. Additionally, under various rainfall scenarios in a typical year, the carbon emission reduction effect of sponge city construction exceeded the carbon emissions, achieving carbon neutrality within 22 to 30 years of operation. This demonstrates that the carbon emission reduction effect of sponge city communities is significant. The findings of this study provide data and a theoretical basis for the low-carbon construction of sponge cities in China.