Mechanical and strain sensing capabilities of carbon nanotube (CNT) reinforced composites manufactured by digital light processing (DLP) 3D printing technology have been studied. Both CNT content and a post-curing treatment effects have been analyzed. It has been observed that post-curing treatment has a significant influence on mechanical properties, with an increase of Young’s modulus and glass transition temperature whereas their effect in electrical properties is not so important. Furthermore, the strain sensing tests show a linear response of electrical resistance with applied strain, with higher values of sensitivity when decreasing CNT content due to a higher interparticle distance. Moreover, the electrical sensitivity of bending tests is significantly lower than in tensile ones due to the compression subjected face effect. Therefore, the good gauge factor values (around 2–3) and the high linear response proves the applicability of the proposed nanocomposites in structural health monitoring applications.

The strain-sensing, self-curing and self-heating capabilities of a 3D printed circuit made of a graphene nanoplatelet and carbon nanotube reinforced resin, have been widely explored. These materials exhibit high Joule’s heating effect capabilities that can be used for post-curing processes. More specifically, the values of glass transition temperature reached by Joule’s heating post-curing were very similar to those obtained by conventional oven heating. The temperature profile along each individual ribbon was relatively homogeneous, being an indicative of a good nanoparticle dispersion, confirmed by field emission gun scanning electron microscope analysis. Furthermore, the proposed printed circuits showed excellent strain-sensing capabilities with a much higher strain sensitivity, with a gauge factor of 6–8, in comparison to conventional metallic gauges or bulk nanocomposites, with a gauge factor of around 2, showing also good linearity. In addition, the breakage of individual ribbons can be easily detected by the strain-sensing system as a sharp increase of the electrical resistance. Finally, temperature compensation tests showed that, in case of printed ribbon breakage, it is possible to keep constant the average temperature of the circuit by raising the applied voltage to avoid ice accretion. Thus, with none to two broken ribbons, the 3D printed circuit can act as an efficient anti-icing and de-icing system.

Electromechanical sensing devices, based on resins doped with carbon nanotubes, were developed by digital light processing (DLP) 3D printing technology in order to increase design freedom and identify new future and innovative applications. The analysis of electromechanical properties was carried out on specific sensors manufactured by DLP 3D printing technology with complex geometries: a spring, a three-column device and a footstep-sensing platform based on the three-column device. All of them show a great sensitivity of the measured electrical resistance to the applied load and high cyclic reproducibility, demonstrating their versatility and applicability to be implemented in numerous items in our daily lives or in industrial devices. Different types of carbon nanotubes—single-walled, double-walled and multi-walled CNTs (SWCNTs, DWCNTs, MWCNTs)—were used to evaluate the effect of their morphology on electrical and electromechanical performance. SWCNT- and DWCNT-doped nanocomposites presented a higher T_g compared with MWCNT-doped nanocomposites due to a lower UV light shielding effect. This phenomenon also justifies the decrease of nanocomposite T_g with the increase of CNT content in every case. The electromechanical analysis reveals that SWCNT- and DWCNT-doped nanocomposites show a higher electromechanical performance than nanocomposites doped with MWCNTs, with a slight increment of strain sensitivity in tensile conditions, but also a significant strain sensitivity gain at bending conditions.

The shape memory (SM) capabilities of nanocomposites based on two photocurable acrylated/methacrylated resins, doped with carbon nanotubes (CNTs), and manufactured by digital light processing 3D printing were investigated. The mechanical properties and glass transition temperature (T_g) can be tailored in a broad range by varying the weight ratio of the two resins (T_g ranging from 15 to 190 °C; Young’s modulus from 1.5 to 2500 MPa). Shape fixity (S_F) and recovery (S_R) ratios are strongly influenced by the temperature being significantly higher at temperatures close to the T_g. The results confirm that the S_F strongly depends on the stiffness of chain segments between cross-linking points, whereas the S_R mainly depends on the cross-link density of the network. CNT addition barely affects the S_F and S_R in the conventional oven, whereas the recovery speed using IR heating is significantly increased for the doped nanocomposites due to their higher IR absorbance.

The present study focuses on the multifunctional capabilities of carbon nanotube (CNT)-reinforced vitrimers. More specifically, the thermomechanical properties, the Joule effect heating capabilities, the electrical conductivity, the shape memory, and the chemical recycling capacity are explored as a function of the CNT content and the NH₂/epoxy ratio. It is observed that the electrical conductivity increases with the CNT content due to a higher number of electrical pathways, while the effect of the NH₂/epoxy ratio is not as prevalent. Moreover, the T_g of the material decreases when increasing the NH₂/epoxy ratio due to the lower cross-link density, whereas the effect of the CNTs is more complex, in some cases promoting a steric hindrance. The results of Joule heating tests prove the suitability of the proposed materials for resistive heating, reaching average temperatures above 200 °C when applying 100 V for the most electrically conductive samples. Shape memory behavior shows an outstanding shape fixity ratio in every case (around 100%) and a higher shape recovery ratio (95% for the best-tested condition) when decreasing the NH₂/epoxy ratio and increasing the CNT content, as both hinder the rearrangement of the dynamic bonds. Finally, the results of the recyclability tests show the ability to regain the nanoreinforcement for their further use. Therefore, from a multifunctional analysis, it can be stated that the proposed materials present promising properties for a wide range of applications, such as Anti-icing and De-icing Systems (ADIS), Joule heating devices for comfort or thermotherapy, or self-deployable structures, among others.