A new generation of porous polymer networks, PPNs, has been obtained in quantitative yield by reacting in superacidic media two rigid trifunctional aromatic monomers (1,3,5-triphenylbenzene and triptycene) with two ketones having electron-withdrawing groups (trifluoroacetophenone and isatin). The resulting amorphous networks are microporous materials, with moderate BET surface areas (from 580 to 790 m2 g-1) and have high thermal stability. In particular, isatin yields networks with a very high narrow microporosity contribution, 82% for triptycene and 64% for 1,3,5-triphenylbenzene. The existence of favorable interactions between lactams and CO2 molecules has been stated. The materials show excellent CO2 uptakes (up to 207 mg g-1 at 0 ºC/1 bar) and can be regenerated by vacuum, without heating. Under post-combustion conditions, their CO2/N2 selectivities are comparable to those of other organic porous networks. Because of the easily scalable synthetic method and their favorable characteristics, these materials are very promising as industrial adsorbents.

A series of new organic polyimides were synthesized from 4-fluoro-4'4"-diaminotriphenylmethane and four different aromatic dianhydrides through a one-step, high-temperature, direct polycondensation in m-cresol at 180–200 °C, resulting in the formation of high-molecular-weight polyimides (inherent viscosities ~ 1.0–1.3 dL/g). All the resulting polyimides exhibited good thermal stability with initial decomposition temperatures above 434 °C, glass-transition temperatures between 285 and 316 °C, and good solubility in polar aprotic solvents. Wide-angle X-ray scattering data indicated that the polyimides were amorphous. Dense membranes were prepared by solution casting and solvent evaporation to evaluate their gas transport properties (permeability, diffusivity, and solubility coefficients) toward pure hydrogen, helium, oxygen, nitrogen, methane, and carbon dioxide gases. In general, the gas permeability was increased as both the fractional free volume and d-spacing were also increased. A good combination of permeability and selectivity was promoted efficiently by the bulky hexafluoroisopropylidene and 4-fluoro-phenyl groups introduced into the polyimides. The results indicate that the gas transport properties of these films depend on both the structure of the anhydride moiety, which controls the intrinsic intramolecular rigidity, and the 4-fluoro-phenyl pendant group, which disrupts the intermolecular packing.