Inverted (pin) perovskite solar cells (PSCs) afford improved operating stability in comparison to their nip counterparts but have lagged in power conversion efficiency (PCE). The energetic losses responsible for this PCE deficit in pin PSCs occur primarily at the interfaces between the perovskite and the charge-transport layers. Additive and surface treatments that use passivating ligands usually bind to a single active binding site: This dense packing of electrically resistive passivants perpendicular to the surface may limit the fill factor in pin PSCs. We identified ligands that bind two neighboring lead(II) ion (Pb ²⁺ ) defect sites in a planar ligand orientation on the perovskite. We fabricated pin PSCs and report a certified quasi–steady state PCE of 26.15 and 24.74% for 0.05– and 1.04–square centimeter illuminated areas, respectively. The devices retain 95% of their initial PCE after 1200 hours of continuous 1 sun maximum power point operation at 65°C.

We have studied friction and dissipation in single and bilayer graphene films grown epitaxially on SiC. The friction on SiC is greatly reduced by a single layer of graphene and reduced by another factor of 2 on bilayer graphene. The friction contrast between single and bilayer graphene arises from a dramatic difference in electron-phonon coupling, which we discovered by means of angle-resolved photoemission spectroscopy. Bilayer graphene as a lubricant outperforms even graphite due to reduced adhesion.

The work function difference between single layer and bilayer graphene grown epitaxially on $6H\text{-SiC}\left(0001\right)$ has been determined to be $135\pm 9\text{meV}$ by means of the Kelvin probe force microscopy. Bilayer films are found to increase the work function as compared to single layer films. This method allows an unambiguous distinction between interface layer, single layer, and bilayer graphene. In combination with high-resolution topographic imaging, the complex step structure of epitaxial graphene on SiC can be resolved with respect to substrate and graphene layer steps.