Fungal delignification can be a feasible process to pretreat biomass for bioethanol production if its performance is improved in terms of efficiency through a few modifications. The aim of this study was to enhance the biodelignification pretreatment of rice straw using laccase in the presence of ionic liquid (1-Allyl-3-methylimidazolium chloride, [AMIM]Cl) or surfactant (TritonX-100). Addition of 750 mg/L [AMIM]Cl and 500 mg/L TritonX-100 increases the lignin removal to 18.49% and 31.79%, which is higher than that of laccase only (11.97%). The enzymatic saccharification process was carried out based on different strategies. The highest cellulose conversion, 40.96%, 38.24%, and 37.91%, was obtained after 72 h of enzymatic saccharification when the substrate was washed with distilled water after pretreatment of rice straw with laccase + TritonX-100, laccase + [AMIM]Cl, and laccase only, respectively. In addition, the morphology and structure changes of pretreated and untreated rice straw were studied. Both surface area and cellulose crystallinity are substantially altered after laccase + [AMIM]Cl and laccase + TritonX-100 pretreatment. Enhanced saccharification efficiency of rice straw was achieved by laccase pretreatment with ionic liquid or surfactant in a single system.

In this study, electrodes of titanium dioxide nanotube arrays (TNAs) were successfully synthesized by applying the anodic oxidation etching method, as well as the use of green synthetic technology to add reducing agents of tea or coffee to reduce metal palladium from palladium chloride. Synthesis of palladium modified TNAs (Pd/TNAs) was conducted by the microwave hydrothermal method after the metal palladium was reduced. In order to identify the surface structure, light absorption and elemental composition, TNAs and Pd/TNAs were characterized by X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD). Furthermore, to test the photocurrent density, electron resistance, and hydroxyl radicals by I-t plot, electrochemistry impedance spectroscopy (EIS), and electron paramagnetic resonance (EPR) were investigated. The photocurrent (4.0 mA/cm²) of Pd/TNAs-C (using coffee as the reducing agent) at +1.0 V (vs. Ag/AgCl) was higher than that of the pure TNAs (1.5 mA/cm²), illustrating that Pd/TNAs-C can effectively separate photogenerated electrons and holes. Pd/TNAs is a favorable material as a photoanode for the photoelectrochemical (PEC) removal of organic pollutants in wastewater.

Atmospheric particulate matters (PMs) were measured in an industry-intensive region in central Taiwan in order to investigate the characteristics and possible sources of PMs. The samplings were simultaneously conducted using a 10- and 3-stage Micro Orifice Uniform Deposit Impactor (MOUDI) from 2017 to 2018. In this study, the characteristics of PMs in this region were evaluated by measuring the mass concentration of PMs and analyzing water-soluble ions and metallic elements, as well as dioxins. Additionally, principal component analysis (PCA) was used to identify the potential sources of PMs. The results showed that the mean concentration of coarse (>1.8 μm), fine (0.1–1.8 μm), and ultrafine (<0.1 μm) particles were 13.60, 14.38, and 3.44 μg/m³, respectively. In the industry-intensive region, the size distribution of ambient particles showed a bi-modal distribution with a high concentration of coarse particles in the spring and summer, while fine particles were dominant in the autumn and winter. The most abundant water-soluble ions of PMs were NO₃⁻, Cl⁻, and SO₄²⁻, while the majority of metallic elements were Na, Fe, Ca, Al, and Mg in different particle sizes. The results of Pearson’s correlation analysis for metals indicated that the particles in the collected air samples were related to the iron and steelmaking industries, coal burning, vehicle exhausts, and high-tech industries. The dioxin concentration ranged from 0.0006 to 0.0017 pg I-TEQ/Nm³. Principal component analysis (PCA) revealed that the contribution to PMs was associated with sea salt, secondary pollutants, and industrial process.

This study used iron modified titanate nanotube arrays (Fe/TNAs) to remove E. coli in a photoelectrochemical system. The Fe/TNAs was synthesized by the anodization method and followed by the square wave voltammetry electrochemical deposition (SWVE) method with ferric nitrate as the precursor. Fe/TNAs were characterized by SEM, XRD, XPS, and UV-vis DRS to investigate the surface properties and light absorption. As a result, the iron nanoparticles (NPs) were successfully deposited on the tubular structure of the TNAs, which showed the best light utilization. Moreover, the photoelectrochemical (PEC) properties of the Fe/TNAs were measured by current-light response and electrochemical impedance spectroscopy. The photocurrent of the Fe/TNAs-0.5 (3.5 mA/cm²) was higher than TNAs (2.0 mA/cm²) and electron lifetime of Fe/TNAs-0.5 (433.3 ms) were also longer than TNAs (290.3 ms). Compared to the photolytic (P), photocatalytic (PC), and electrochemical (EC) method, Fe/TNAs PEC showed the best removal efficiency for methyl orange degradation. Furthermore, the Fe/TNAs PEC system also performed better removal efficiency than that of photolysis method in E. coli degradation experiments.