The co-culture of Cupriavidus necator DSM 428 and Pseudomonas citronellolis NRRL B-2504 was performed using apple pulp waste from the fruit processing industry as the sole carbon source to produce poly(3-hydroxybutyrate), P(3HB) and medium-chain length PHA, mcl-PHA, respectively. The polymers accumulated by both strains were extracted from the co-culture’s biomass, resulting in a natural blend that was composed of around 48 wt% P(3HB) and 52 wt% mcl-PHA, with an average molecular weight of 4.3 × 10⁵ Da and a polydispersity index of 2.2. Two melting temperatures (T_m) were observed for the blend, 52 and 174 °C, which correspond to the T_m of the mcl-PHA and P(3HB), respectively. P(3HB)/mcl-PHA blend films prepared by the solvent evaporation method had permeabilities to oxygen and carbon dioxide of 2.6 and 32 Barrer, respectively. The films were flexible and easily deformed, as demonstrated by their tensile strength at break of 1.47 ± 0.07 MPa, with a deformation of 338 ± 19% until breaking, associated with a Young modulus of 5.42 ± 1.02 MPa. This study demonstrates for the first time the feasibility of using the co-culture of C. necator and P. citronellolis strains to obtain a natural blend of P(3HB)/mcl-PHA that can be processed into films suitable for applications ranging from commodity packaging products to high-value biomaterials.

Biosurfactants synthesized by microorganisms represent safe and sustainable alternatives to the use of synthetic surfactants, due to their lower toxicity, better biodegradability and biocompatibility, and their production from low-cost feedstocks. In line with this, the present study describes the physical, chemical, and functional characterization of the biopolymer secreted by the bacterium Burkholderia thailandensis DSM 13276, envisaging its validation as a biosurfactant. The biopolymer was found to be a glycolipopeptide with carbohydrate and protein contents of 33.1 ± 6.4% and 23.0 ± 3.2%, respectively. Galactose, glucose, rhamnose, mannose, and glucuronic acid were detected in the carbohydrate moiety at a relative molar ratio of 4:3:2:2:1. It is a high-molecular-weight biopolymer (1.0 × 10⁷ Da) with low polydispersity (1.66), and forms aqueous solutions with shear-thinning behavior, which remained after autoclaving. The biopolymer has demonstrated a good emulsion-stabilizing capacity towards different hydrophobic compounds, namely, benzene, almond oil, and sunflower oil. The emulsions prepared with the biosurfactant, as well as with its autoclaved solution, displayed high emulsification activity (>90% and ~50%, respectively). Moreover, the almond and sunflower oil emulsions stabilized with the biosurfactant were stable for up to 4 weeks, which further supports the potential of this novel biopolymer for utilization as a natural bioemulsifier.