The application of additive manufacturing changes from prototypes to series production. In order to fulfill all requirements of series production, the process and the material characteristics must be known. The machine operator of additive manufacturing systems is both a component and a material producer. Nevertheless, there is no standardized procedure for the manufacturing or testing of such materials. This includes the high degree of anisotropy of additively manufactured polymers via material extrusion. The interlayer bonding performance between two layers in the manufacturing direction z is the obvious weakness that needs to be improved. By optimizing this interlayer contact zone, the overall performance of the additively manufactured polymer is increased. This was achieved by process modification with an infrared preheating system (IPS) to keep the temperature of the interlayer contact zone above the glass transition temperature during the manufacturing process. Combining destructive and non-destructive testing methods, the process modification IPS was determined and evaluated by a systematic approach for characterizing the interlayer bonding performance. Thereby, tensile tests under quasi-static and cyclic loading were carried out on short carbon fiber-reinforced polyamide (SCFRP). In addition, micro-computed tomography and microscopic investigations were used to determine the process quality. The IPS increases the ultimate interlayer tensile strength by approx. 15% and shows a tendency to significantly improved the fatigue properties. Simultaneously, the analysis of the micro-computed tomography data shows a homogenization of the void distribution by using the IPS.

Additive manufacturing of polymers via material extrusion and its future applications are gaining interest. Supporting the evolution from prototype to serial applications, additional testing conditions are needed. The additively manufactured and anisotropic polymers often show a weak point in the interlayer contact area in the manufacturing direction. Different process parameters, such as layer height, play a key role for generating the interlayer contact area. Since the manufacturing productivity depends on the layer height as well, a special focus is placed on this process parameter. A small layer height has the objective of achieving better material performance, whereas a larger layer height is characterized by better economy. Therefore, the capability- and economy-oriented variation was investigated for strain rates between 2.5 and 250 s⁻¹ under tensile and shear load conditions. The test series with dynamic loadings were designed monitoring future applications. The interlayer tensile tests were performed with a special specimen geometry, which enables a correction of the force measurement. By using a small specimen geometry with a force measurement directly on the specimen, the influence of travelling stress waves, which occur due to the impact at high strain rates, is reduced. The interlayer tensile tests indicate a strain rate dependency of additively manufactured polymers. The capability-oriented variation achieves a higher ultimate tensile and shear strength compared to the economy-oriented variation. The external and internal quality assessment indicates an increasing primary surface profile and void volume content for increasing the layer height.