An 18-Ni 300 grade maraging steel was processed by selective laser melting and an investigation was carried out on microstructural and mechanical behaviour as a function of aging condition. Owing to the rapid cooling rate, the as-built alloy featured a full potential for precipitate strengthening, without the need of a solution treatment prior to aging. The amount of reversed austenite found in the microstructure increased after aging and revealed to depend on aging temperature and time. Similarly to the corresponding wrought counterpart, also in the selective laser-melted 18-Ni 300 alloy, aging promoted a dramatic increase in strength with respect to the as-built condition and a drop in tensile ductility. No systematic changes were found in tensile properties as a function of measured amount of austenite. It is proposed that the submicrometric structure and the phase distribution inherited by the rapid solidification condition brought by selective laser melting are such that changes in tensile strength and ductility are mainly governed by the effects brought by the strengthening precipitates, whereas the concurrent reversion of the γ-Fe phase in different amounts seems to play a minor role.

Al-Si-Cu foundry alloys are widely applied in the form of high-pressure diecast components. They feature hypo- or nearly eutectic compositions, such as AlSi9Cu3(Fe), AlSi11Cu2(Fe), and AlSi12Cu1(Fe) alloys, which are used in the present study. Diecast specimens, with a thickness of 3 mm, were used for tension tests. The short-term mechanical behavior was characterized at temperatures from 25 up to 450 °C. At temperatures above 200 °C, the tensile strength properties (YS and UTS) of the investigated alloys were severely affected by temperature, and less by chemical differences. Material hardness and ductility indexes better highlighted the differences in the mechanical behavior of these age-hardenable alloys and allowed us to relate them to the microstructure and its changes that took place at test temperatures. Thermodynamic calculations were found to be useful tools to predict phases formed during solidification, as well as those related to precipitation strengthening. By means of the performed comprehensive material characterization, deeper knowledge of the microstructural changes of Al-Si-Cu foundry alloys during short-term mechanical behavior was obtained. The gained knowledge can be used as input data for constitutive modeling of the investigated alloys.