In the article has been presented an analysis of susceptibility of selected dental materials, made in the CAD/CAM technology. The morphology and structural properties of selected dental materials and their composites were determined by using XRPD (X-ray powder diffraction) techniques, as well as the IR (infrared) spectroscopy. Moreover, an adhesion as well as development of biofilm by oral microorganisms has been studied. It has been shown that a degree of the biofilm development on the tested dental materials depended on microorganism genus and species. Streptococcus mutans has demonstrated the best adhesion to the tested materials in comparison with Candida albicans and Lactobacillus rhamnosus. However, the sintered materials such as IPS e.max® and the polished IPS e.max® have showed the best “anti-adhesive properties” in relation to S. mutans and L. rhamnosus that have not formed the biofilm on the polished IPS e.max® sample. Furthermore, S. mutans have not formed the biofilm on both surfaces. On the contrary to S. mutans and L. rhamnosus, C. albicans has demonstrated the adhesive properties in relation to the above-mentioned surfaces. Moreover, in contrast to S. mutans and C. albicans, L. rhamnosus has not formed the biofilm on the polished IPS Empress material.

The purpose of the in vitro study presented in this paper was to determine the long-term release of fluoride ions from selected ormocer materials (Admira (A), Admira Flow (AF), Admira Seal (AS)). The release of fluoride ions from these materials into a saline solution (0.9% NaCl) and deionized water was tested for 14 weeks. In a long-term study the measurements were taken after 1 and 3 h, then 1, 2, and 3 days and then at weekly intervals for 14 weeks. In a short-term study the measurements were made after 3, 24, 48, 72, 69, 168 h, i.e., within 7 days. All materials used in the test showed a constant level of fluoride release. The highest level of cumulative release of fluoride ions into deionized water was found in the AS material (23.95 ± 4.30 μg/mm²), slightly lower in the A material (23.26 ± 4.16 μg/mm²) and the lowest in the AF material (16.79 ± 2.26 μg/mm²). The highest level of cumulative release into saline solution was found in AF (8.08 ± 1.30 μg/mm²), slightly lower in AS (7.36 ± 0.30 μg/mm²) and the lowest in A (6.73 ± 1.10 μg /mm²). After 1 h of immersion of the samples in the saline solution, the highest level of fluoride was released by AF (0.57 ± 0.06 μg/mm²) followed by A (0.20 ± 0.03 μg/mm²) and AS (0.19 ± 0.02 µg/mm²). Moreover, in the 14-week study, the total amount of fluoride release into the saline, which imitates the environment of the oral cavity, was observed as the highest in the AF sample.

The purpose of this study was to present the level of bone tissue deformation after drilling under variable conditions in three different dental implant systems in a microscopic analysis. Straumann, Osstem, and S-Wide systems were used to drill boreholes in 27 porcine ribs at three different rotation speeds and under three different cooling conditions. The material was analyzed using a Nikon 80i microscope. The analysis concerned the morphological quality of the obtained boreholes. The statistical analysis revealed that satisfactory results in all drilling systems were obtained when the rotational speed did not exceed 800 revolutions per minute (rpm) regardless of the cooling temperature. However, increased rotational speed and cooling at 4 °C produced better results than without cooling in all the tested systems. Different implant systems have unique drill geometry and therefore generate differences in tissue damage under various conditions. In the experiment, a sufficient required structure was obtained in all systems, but the Straumann system yielded the best results under all the examined conditions.

Purpose. The aim of this work was to compare the temperature fluctuations that occur during the development of the implant bed using three different implant systems and the impact on their value of cooling method and rotational speed of drill. Material and Methods. As a model of the human jaw due to the analogy of bone structure and hardness, pig ribs were used. Drills from three different implant systems were used in the study: Straumann® (Straumann GmbH, Basel, Switzerland), AnyRidge® (Megagen Implant Co., Ltd., Daegu, South Korea), and Osstem (OSSTEM IMPLANT CO., LTD., Seoul, South Korea). The sequence of three successive drills was given—from pilot drill to final drill. For each system, a group with two water cooling methods, without cooling, and three different speed ranges, 800, 1200, and 1500 rpm, and their effect on temperature fluctuations was evaluated. The temperature was measured by thermography. Results. The highest temperature increases were noted during preparation with pilot drills. The maximum temperature (50.8°C) was noted for the AnyRidge pilot drill at 1500 rpm without cooling. When cooling with physiological saline, none of the applied drills exceeded 28°C. Significant differences between lack of cooling and cooling with saline at 20°C and 3°C have been demonstrated. During preparation with cooling, the difference between the times of the maximum temperature achievement was observed between AnyRidge® and Osstem (2.6 vs. 1.6 s, p = 0.004). Conclusion. The experiment showed that the drills of the tested implant systems differed in the amount of heat generated during operation. The temperature of the cooling solution and the rotational speed applied have an influence on its amount.

The aim of this article was to present a characteristic clinical image of Melnick–Needles syndrome using an example of an 11.5‐year‐old female patient treated at the Facial Congenital Disorders Outpatient Clinic as well as to present the actual literature review of the surgical treatment. The patient was diagnosed with several characteristics typical for Melnick–Needles syndrome: single‐sided hearing loss, malocclusion, and facial dysmorphism, among others. Due to malocclusion and facial dysmorphism, the patient with Melnick–Needles syndrome requires orthodontic treatment with surgical intervention. Mandibular distraction with fixed appliance treatment is a recommended treatment protocol.

Introduction: Teeth intended for use as autogenous augmentative material may carry microbiological contamination, which can compromise the safety of regenerative procedures in the oral cavity. Therefore, effective disinfection protocols are crucial to ensure the microbiological purity of dentin-derived graft materials. Objective: This study aimed to evaluate the effectiveness of a 30% alkaline ethanol solution containing 0.5 M sodium hydroxide in eliminating microorganisms from dentin material intended for autogenous augmentation. Materials and Methods: The study included 44 extracted teeth that were processed using the Smart Dentin Grinder procedure. The presence of microorganisms was analysed using standard microbiological methods before and after treatment with the disinfectant solution. Additionally, the potential association between tooth eruption status and the effectiveness of the disinfection process was evaluated using Fisher’s exact test, with odds ratios calculated using the Haldane–Anscombe correction to address zero cell counts. Results: Processing dentin in a 30% alkaline ethyl alcohol solution containing 0.5 M sodium hydroxide is an effective method for eliminating microorganisms, thereby rendering the material completely microbiologically pure. Conclusions: The dentine processing procedure used appears to ensure the production of autogenous material free from microbiological contamination, indicating its potential safety in clinical applications.