Herein, the size dependent behavior of cobalt ferrite nanoparticles was investigated using synchrotron radiation based techniques. Scanning electron micrographs revealed the enhancement of particle/crystallite size with increase of annealing temperature. Moreover, the shape of these particles also changed with increase of crystallite size. Saturation magnetization increased with increase of crystallite size. The higher saturation magnetization for larger crystallite size nanoparticles was attributed to a cation distribution similar to that of bulk CoFe₂O₄. The optical band-gap of these nanoparticles decreased from 1.9 eV to 1.7 eV with increase of crystallite size. The enhancement of the optical band-gap for smaller crystallites was due to phenomena of optical confinement occurring in the nanoparticles. Fe L Co L-edge near edge extended X-ray absorption fine structure (NEXAFS) measurements showed that Fe and Co ions remain in the 3+ and 2+ state in these nanoparticles. The results obtained from Fe & Co K-edge X-ray absorption near edge structure (XANES)-imaging experiments further revealed that this oxidation state was possessed by even the crystallites. Extended X-ray absorption fine structure (EXAFS) measurements revealed distribution of Fe and Co ions among tetrahedral (A) and octahedral (B) sites of the spinel structure which corroborates the results obtained from Rietveld refinement of X-ray diffraction patterns (XRD). X-ray magnetic circular di-chroism (XMCD) measurements revealed negative exchange interaction among the ions situated in tetrahedral (A) and octahedral (B) sites. Theoretical and experimental calculated magnetic moments revealed the dominancy of size effects rather than the cation redistribution in the spinel lattice of CoFe₂O₄ nanoparticles.

Herein, we report the soft X-ray absorption spectroscopic investigation for Li(Ni_0.8Co_0.1Mn_0.1)O₂ cathode material during charging and discharging. These measurements were carried out at the Mn L-, Co L-, and Ni L-edges during various stages of charging and discharging. Both the Mn and Co L-edge spectroscopic measurements reflect the invariance in the oxidation states of Mn and Co ions. The Ni L-edge measurements show the modification of the oxidation state of Ni ions during the charging and discharging process. These studies show that e_g states are affected dominantly in the case of Ni ions during the charging and discharging process. The O K-edge measurements reflect modulation of metal–oxygen hybridization as envisaged from the area-ratio variation of spectral features corresponding to t_2g and e_g states.

High-energy radiation sources have provided a strong security inspection capability using a non-invasive imaging system. The use of multiple radiation sources in one imaging system can also lead to a more powerful system that can classify various materials compared to using a single radiation source. The Advanced Radiation Technology Institute of Korea Atomic Energy Research Institute has developed an air cargo inspection system using multiple radiation sources such as fast neutrons and gamma-rays to classify the plastics, metals, and organics among various sample materials. The fast neutron beam with an energy of 14.1 MeV, generated using the D-T neutron generator, and the gamma-ray beam with an energy of 6 MeV, generated by an electron linear accelerator, are projected onto the vertically aligned scintillator-based radiation detectors. The neutron and gamma-ray images of a cargo container moved by a motorized linear translation stage are acquired, and the image data processing shows good material classification results. In this paper, we describe a multi-radiation imaging system for air cargo inspection and investigate its material classification capability using various sample materials.

Background: A nondestructive test is commonly used to inspect the surface defects and internal structure of an object without any physical damage. X-rays generated from an electron accelerator or a tube are one of the methods used for nondestructive testing. The high penetration of X-rays through materials with low atomic numbers makes it difficult to discriminate between these materials using X-ray imaging. The interaction characteristics of neutrons with materials can supplement the limitations of X-ray imaging in material discrimination.Materials and Methods: The radiation image acquisition process for air-cargo security inspection equipment using X-rays and neutrons was simulated using a GEometry ANd Tracking (Geant4) simulation toolkit. Radiation images of phantoms composed of 13 materials were obtained, and the R-value, representing the attenuation ratio of neutrons and gamma rays in a material, was calculated from these images.Results and Discussion: The R-values were calculated from the simulated X-ray and neutron images for each phantom and compared with those obtained in the experiments. The R-values obtained from the experiments were higher than those obtained from the simulations. The difference can be due to the following two causes. The first reason is that there are various facilities or equipment in the experimental environment that scatter neutrons, unlike the simulation. The other is the difference in the neutron signal processing. In the simulation, the neutron signal is the sum of the number of neutrons entering the detector. However, in the experiment, the neutron signal was obtained by superimposing the intensities of the neutron signals. Neutron detectors also detect gamma rays, and the neutron signal cannot be clearly distinguished in the process of separating the two types of radiation. Despite these differences, the two results showed similar trends and the viability of using simulation-based radiation images, particularly in the field of security screening. With further research, the simulation-based radiation images can replace ones from experiments and be used in the related fields.Conclusion: The Korea Atomic Energy Research Institute has developed air-cargo security inspection equipment using neutrons and X-rays. Using this equipment, radiation images and R-values for various materials were obtained. The equipment was reconstructed, and the R-values were obtained for 13 materials using the Geant4 simulation toolkit. The R-values calculated by experiment and simulation show similar trends. Therefore, we confirmed the feasibility of using the simulation-based radiation image.

The scission rates of polystyrene and fluorinated polystyrene irradiated in an irradiation facility with Co-60 γ-rays were determined using molecular dynamics simulation and gel permeation chromatography (GPC) molecular weight distributions. The prediction was based on the assumption that γ-ray energy is transferred to the initial velocity of the primary knock-on atom. We employed a molecular dynamics simulation procedure to compute the changes in bond length between the connections for selected values of the absorbed dose and compared the calculated values with measurements made on the irradiated samples. The samples were exposed to four different absorbed doses of 25, 50, 75, and 100 kGy. The scission process and scission ratio were simulated with LAMMPS with ReaxFF potential for each bond, and we compared the simulation results with the experimental data especially measuring average molecular weight to evaluate the effect of fluorination on radiation enhancement.