In the present study, pomegranate peel extract was used as a reinforcing agent in developing chitosan-based edible film. Different concentrations (0.2 g/mL, 0.4 g/mL, 0.6 g/mL, 0.8 g/mL, and 1.0 g/mL) of pomegranate peel extract were incorporated in chitosan-based edible film. A neat chitosan film was used as a control. This work covers the effect of pomegranate peel extract on the physical, biological, mechanical, thermal, and barrier properties of enriched chitosan-based edible film. The results showed that the thickness (0.142–0.159 mm), tensile strength (32.45–35.23 MPa), moisture (11.23–15.28%), opacity (0.039–0.061%), water (1.32–1.60 g·mm/m²), gas barrier properties (93.81–103.45 meq/kg), phenolic content (5.75–32.41 mg/g), and antioxidant activity (23.13–76.54%) of the films increased with increasing volume fraction of pomegranate peel extract. A higher concentration of incorporated pomegranate peel extracts significantly (p < 0.05) reduced the thermal stability of the film, along with its transparency, solubility, swelling, and color. This work revealed that the incorporation of a higher portion of pomegranate peel extract in chitosan film holds significant (p < 0.05) potential for the increase in biological activities of such films in terms of antioxidant and antimicrobial behavior. The properties of pomegranate peel extract-enriched chitosan films could be an excellent cure for free radicals, whereas they could also inhibit the growth of the foodborne pathogens during the processing and preservation of the food. Further studies are needed for the application of pomegranate peel extract-enriched edible films on food products such as fruits and vegetables in order to extend their storage life and improve the quality and safety of preserved food products.

The polysaccharide based composite biomaterial (coating) used in preserving fruits and vegetables during storage is attracting increased attention as it is biodegradable material that prolongs shelf life. In the present investigation, chitosan–pullulan (50:50) composite edible coating was prepared with pomegranate peel extract (0.02 g/mL) as an active antioxidant agent. The effect of treatment with pomegranate peel extract enriched chitosan–pullulan composite edible coating on the shelf life of mango fruits during 18 days of storage period at room (23 °C) and cold (4 °C) temperature was evaluated. Results of the present study demonstrated that the application of chitosan–pullulan composite edible coating significantly (p ≤ 0.05) influences the storage life of mango fruits at both storage temperatures. The chitosan–pullulan composite edible coating reduced the physiological loss in weight (PLW), and maintained total soluble solids (TSS), acidity and pH of coated mango fruits as compared to the control. In addition, fruit sensory quality such as freshness, color, taste and texture were also retained by the treatment. Furthermore, sustained firmness, phenolic content and antioxidant activity confirmed the effectiveness of the pomegranate peel extract enriched chitosan–pullulan composite edible coating on mango fruits. The phenolic, flavonoid and antioxidant activity of coated fruits were retained by pomegranate peel rich edible coating. Therefore, the chitosan–pullulan (50:50) combination with pomegranate peel extract can be used as an alternative preservation method to prolong the shelf life of mango fruits at room and cold storage conditions. However, more in-depth studies are required at farm and transit level without affecting the postharvest quality of mango fruits, providing more revenue for farmers and minimizing postharvest losses.