The addition of an antibacterial agent to dental implants may provide the opportunity to decrease the percentage of implant failures due to peri-implantitis. For this purpose, in this study, the potential efficacy of nanosilver-doped titanium biomaterials was determined. Titanium disks were incorporated with silver nanoparticles over different time periods by Tollens reaction, which is considered to be an eco-friendly, cheap, and easy-to-perform method. The surface roughness, wettability, and silver release profile of each disc were measured. In addition, the antibacterial activity was also evaluated by using disk diffusion tests for bacteria frequently isolated from the peri-implant biofilm: Streptococcus mutans, Streptococcus mitis, Streptococcus oralis, Streptococcus sanguis, Porphyromonas gingivalis, Staphylococcus aureus, and Escherichia coli. Cytotoxicity was evaluated in vitro in a natural human osteoblasts cell culture. The addition of nanosilver significantly increased the surface roughness and decreased the wettability in a dose-dependent manner. These surfaces were significantly toxic to all the tested bacteria following a 48-hour exposure, regardless of silver doping duration. A concentration of 0.05 ppm was sufficient to inhibit Gram-positive and Gram-negative species, with the latter being significantly more susceptible to silver ions. However, after the exposure of human osteoblasts to 0.1 ppm of silver ions, a significant decrease in cell viability was observed by using ToxiLight™ BioAssay Kit after 72 hours. Data from the present study indicated that the incorporation of nanosilver may influence the surface properties that are important in the implant healing process. The presence of nanosilver on the titanium provides an antibacterial activity related to the bacteria involved in peri-implantitis. Finally, the potential toxicological considerations of nanosilver should further be investigated, as both the antibacterial and cytotoxic properties may be observed at similar concentration ranges.

Calcium phosphates, due to their similarity to the inorganic fraction of mineralized tissues, are of great importance in treatment of bone defects. In order to improve the biological activity of hydroxyapatite (HAP), its fluoride-substituted modification (FAP) was synthesized using the sol-gel method and calcined at three different temperatures in the range of 800-1200 °C. Physicochemical and biological properties were evaluated to indicate which material would support bone regeneration the best. X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy dispersive X-ray spectrometry (EDS), and Fourier transform infrared spectroscopy (FTIR) revealed that fluoride ions were incorporated into the apatite lattice structure. In studies it was found that fluorapatite sintered at the highest temperature had the lowest porosity, no internal pores and the highest density. In vitro ion reactivity assessments showed that during the 28-day immersion of the samples in the simulated body fluid, the uptake of calcium and phosphorus ions was inversely correlated to the calcination temperature. All tested materials were non-toxic since the cytotoxicity MTT assay demonstrated that the viability of preosteoblast cells incubated with sample extracts was high. Fluorapatite sintered at 800 °C was determined to be of optimal porosity and fluoride release capacity and then used in cell proliferation studies. The results showed that it significantly shortened the doubling time and thus enhanced the proliferation of osteogenic cells, as compared to the fluoride solutions and control group. Therefore, this material is proposed for the use in orthopedic applications and bone tissue engineering.

Aim: The studies on tooth structure provided basis for nanotechnology-based dental treatment approaches known as nanodentistry which aims at detection and treatment of oral pathologies, such as dental caries and periodontal diseases, insufficiently being treated by conventional materials or drugs. This review aims at defining the role of nanodentistry in the medical area, its potential and hazards. Materials & methods: To validate these issues, current literature on nanomaterials for dental applications was critically reviewed. Results: Nanomaterials for teeth restoration, bone regeneration and oral implantology exhibit better mechanical properties and provide more efficient esthetic outcome. However, still little is known about influence of long-term function of such biomaterials in the living organism. Conclusion: As application of nanomaterials in industry and medical-related sciences is still expanding, more information is needed on how such nano-dental materials may interfere with oral cavity, GI tra...