Surface modification of polysulfone ultrafiltration membranes was performed via addition of an anionic polymer flocculant based on acrylamide and sodium acrylate (PASA) to the coagulation bath upon membrane preparation by non-solvent induced phase separation (NIPS). The effect of PASA concentration in the coagulant at different coagulation bath temperatures on membrane formation time, membrane structure, surface roughness, hydrophilic-hydrophobic balance of the skin layer, surface charge, as well as separation and antifouling performance was studied. Scanning electron microscopy (SEM), atomic force microscopy (AFM), Fourier transform infrared (FTIR) spectroscopy, contact angle and zeta potential measurements were utilized for membrane characterization. Membrane barrier and antifouling properties were evaluated in ultrafiltration of model solutions containing human serum albumin and humic acids as well as with real surface water. PASA addition was found to affect the kinetics of phase separation leading to delayed demixing mechanism of phase separation due to the substantial increase of coagulant viscosity, which is proved by a large increase of membrane formation time. Denser and thicker skin layer is formed and formation of macrovoids in membrane matrix is suppressed. FTIR analysis confirms the immobilization of PASA macromolecules into the membrane skin layer, which yields improvement of hydrophilicity and change of zeta potential. Modified membrane demonstrated better separation and antifouling performance in the ultrafiltration of humic acid solution and surface water compared to the reference membrane.

A novel method for one-step preparation of antifouling ultrafiltration membranes via a non-solvent induced phase separation (NIPS) technique is proposed. It involves using aqueous 0.05–0.3 wt.% solutions of cationic polyelectrolyte based on a copolymer of acrylamide and 2-acryloxyethyltrimethylammonium chloride (Praestol 859) as a coagulant in NIPS. A systematic study of the effect of the cationic polyelectrolyte addition to the coagulant on the structure, performance and antifouling stability of polysulfone membranes was carried out. The methods for membrane characterization involved scanning electron microscopy (SEM), atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FTIR), contact angle and zeta-potential measurements and evaluation of the permeability, rejection and antifouling performance in human serum albumin solution and surface water ultrafiltration. It was revealed that in the presence of cationic polyelectrolyte in the coagulation bath, its concentration has a major influence on the rate of “solvent–non-solvent” exchange and thus also on the rate of phase separation which significantly affects membrane structure. The immobilization of cationic polyelectrolyte macromolecules into the selective layer was confirmed by FTIR spectroscopy. It was revealed that polyelectrolyte macromolecules predominately immobilize on the surface of the selective layer and not on the bottom layer. Membrane modification was found to improve the hydrophilicity of the selective layer, to increase surface roughness and to change zeta-potential which yields the substantial improvement of membrane antifouling stability toward natural organic matter and human serum albumin.

This study deals with the development of antifouling ultrafiltration membranes based on polysulfone (PSF) for wastewater treatment and the concentration and purification of hemicellulose and lignin in the pulp and paper industry. The efficient simple and reproducible technique of PSF membrane modification to increase antifouling performance by simultaneous addition of triblock copolymer polyethylene glycol-polypropylene glycol-polyethylene glycol (Synperonic F108, M_n =14 × 10³ g mol⁻¹) to the casting solution and addition of polyacrylic acid (PAA, M_n = 250 × 10³ g mol⁻¹) to the coagulation bath is proposed for the first time. The effect of the PAA concentration in the aqueous solution on the PSF/Synperonic F108 membrane structure, surface characteristics, performance, and antifouling stability was investigated. PAA concentrations were varied from 0.35 to 2.0 wt.%. Membrane composition, structure, and topology were investigated by Fourier-transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The addition of PAA into the coagulation bath was revealed to cause the formation of a thicker and denser selective layer with decreasing its pore size and porosity; according to the structural characterization, an interpolymer complex of the two additives was formed on the surface of the PSF membrane. Hydrophilicity of the membrane selective layer surface was shown to increase significantly. The selective layer surface charge was found to become more negative in comparison to the reference membrane. It was shown that PSF/Synperonic F108/PAA membranes are characterized by better antifouling performance in ultrafiltration of humic acid solution and thermomechanical pulp mill (ThMP) process water. Membrane modification with PAA results in higher ThMP process water flux, fouling recovery ratio, and hemicellulose and total lignin rejection compared to the reference PSF/Synperonic F108 membrane. This suggests the possibility of applying the developed membranes for hemicellulose concentration and purification.

The application of environmentally friendly and energy-efficient membrane processes allows improvement the ecological safety and sustainability of industrial production. However, the effective application of membrane processes requires novel high-performance thin film composite (TFC) membranes based on biopolymers to solve environmental problems. In this work for the first time novel thin film nanocomposite (TFN) membranes based on biopolymer chitosan succinate (ChS) modified with the metal organic framework iron 1,3,5-benzenetricarboxylate (Fe-BTC) were developed for enhanced pervaporation dehydration. The formation of a selective layer of TFN membranes on the porous membrane-support was carried out by two methods—dynamic technique and physical adsorption. The effect of the membrane formation method and Fe-BTC content in ChS layer on the structure and physicochemical properties of TFN membranes was investigated. The developed TFN ChS-based membranes were evaluated in the pervaporation dehydration of isopropanol (12–30 wt.% water). It was found that TFN ChS-Fe-BTC membranes prepared by two methods demonstrated improved permeation flux compared to the reference TFC ChS membrane. The best transport properties in pervaporation dehydration of isopropanol (12–30 wt.% water) were possessed by TFN membranes with 40 wt.% Fe-BTC prepared by dynamic technique (permeation flux 99–499 g m⁻² h⁻¹ and 99.99% water in permeate) and TFN membranes with 5 wt.% Fe-BTC developed by physical adsorption (permeation flux 180–701 g m⁻² h⁻¹ and 99.99% water in permeate).