Hexagonal (2H) silicon (Si) semiconductors have excellent mechanical properties and optically diverse applications due to their structure and quasi-direct bandgap. The 2H-Si has a relatively lower direct band gap of approximately 1.69 eV at the Γ-point in comparison with that of diamond-silicon (i.e. 3.4 eV), but it is not actually a direct bandgap semiconductor. Herein, we report an optical property of wide spectrum light emission in visible and infrared ranges from grown Si crystals with a 2H structure of a ₀ = 0.3824 nm, c ₀ = 0.6257 nm, and c ₀ / a ₀ = 1.6362 corresponding to theoretical predictions and experimental results. Obtained via high-resolution transmission electron microscopy measurements, the crystal structure of the grown 2H Si possesses the only stable form of the 2H structure with the characteristic quasi-direct bandgap, achieved using mixed-source hydride vapor phase epitaxy at about 1200 °C. Raman, photoluminescence, and electroluminescence spectra, Commission International de l’ Eclairage chromaticity coordinates of light emission, lattice parameters, and the quality of the crystals were evaluated and found to correspond with the predicted results. The reported material has potential applications in optoelectronics.

Even though a patterned sapphire substrate (PSS) has been used for the growth of a high-quality epilayer because of its many advantages, it has not been successfully used to grow an AlN epilayer for ultraviolet (UV) light-emitting diodes (LEDs) on a PSS up to now. We report the growth of a high-quality AlN epilayer on a PSS, as a substrate for the manufacture of UV LEDs, by hydride vapor phase epitaxy (HVPE). The X-ray diffraction (XRD) peaks for the AlN epilayer grown on the PSS indicate that crystalline AlN with a wurtzite structure was grown successfully on the PSS. Furthermore, HVPE combining both in situ HVPE technology and liquid-phase epitaxy (LPE) using a mixed source is proposed as a novel method for the growth of a flat AlN epilayer on a PSS.

High Al-composition AlGaN and AlN epilayers were grown directly on Si(111) substrate by a hydride vapor phase epitaxy (HVPE) method with a melted mixed source in a graphite boat set in a source zone with high temperatures of T = 700 and 800 °C, respectively. The presence of the Ga material in the mixed source of Ga and Al promoted the growth of AlN and AlGaN epilayers in the growth zone. When the temperature in the source zone was 800 °C, the crystalline quality of the AlN and AlGaN epilayers increased as the ratio of Ga to Al increased, and the optimum mix ratio of Ga to Al for the growth of AlN epilayers was approximately 0.35–0.42, obtained from a numerical fitting analysis of the X-ray diffraction (XRD) data for these epilayers. It appears that they can be grown directly by our melted-mixed-source HVPE method in a high-temperature source zone.

Although hexagonal (2H) silicon (Si) semiconductors exhibit excellent optical properties owing to their quasi-direct bandgap, their growth conditions, which require extremely high pressures, preclude their widespread use in industrial applications. The current study, therefore, proposes a novel approach for the facile growth of hexagonal Si at atmospheric pressure via a unique phenomenon known as Al-based nano absorber. A mixed-source hydride vapor phase epitaxy (HVPE) method was used for the growth of the hexagonal Si single crystals employing a rapid interaction between GaCl₃, AlCl, and SiCl_n gases at a high temperature of 1200 °C using a source mixture of Ga, Al, and Si. In this process, the Al-based nano absorber was formed, which resulted in the absorbance of Si atoms, rather than the growth of Al-based nano absorber, to form the Si crystals due to the subsequent lack of GaCl₃ and AlCl sources. The hexagonal Si structure of these Si crystals was confirmed using field emission scanning electron microscopy, high-resolution x-ray diffraction spectroscopy, and Raman spectroscopy. Thus, the current study establishes atmospheric pressure mixed-source HVPE as a facile approach for growing various allotropic crystals such as Si, C, or Ge via absorption of other atoms by an Al-based nano absorber.

We developed a vertical-type light-emitting diode (LED) in which the substrate is removed using a hydride vapor phase epitaxy (HVPE) apparatus consisting of a multi-graphite boat filled with a mixed source and a high-temperature ( T ≈ 900 °C) RF heating coil outside the source zone. The new chip-growth process with a significant reduction in the number of production steps is completed in only four steps, namely, photolithography, epitaxial layer growth, sorting, and metallization. We analyze the emission mechanism of these lights from measurement results to validate the characteristics of the light emitted from these vertical-type blue LEDs and white LEDs (WLEDs) without substrates, and propose that this mixed-source HVPE method may be a promising production technique for LEDs.

We prepared InGaN light-emitting diodes (LEDs) with the active layers grown from a mixed source of Ga–In–N materials on an n-type GaN substrate by a selective-area growth method and three fabrication steps: photolithography, epitaxial layer growth, and metallization. The preparation followed a previously developed experimental process using apparatus for mixed-source hydride vapor-phase epitaxy (HVPE), which consisted of a multi-graphite boat, for insulating against the high temperature and to control the growth rate of epilayers, filled with the mixed source on the inside and a radio-frequency (RF) heating coil for heating to a high temperature ( T > 900 °C) and for easy control of temperature outside the source zone. Two types of LEDs were prepared, with In compositions of 11.0 and 6.0% in the InGaN active layer, and room-temperature electroluminescence measurements exhibited a main peak corresponding to the In composition at either 420 or 390 nm. The consecutive growth of InGaN LEDs by the mixed-source HVPE method provides a technique for the production of LEDs with a wide range of In compositions in the active layer.