Due to growing consciousness regarding the environmental impact of fossil-based and non-sustainable materials in construction and building applications, there have been an increasing interest in bio-based and degradable materials in this industry. Due to their excellent chemical and thermo-physical properties for thermal energy storage, bio-based phase change materials (BPCMs) have started to attract attention worldwide for low to medium temperature applications. The ready availability, renewability, and low carbon footprint of BPCMs make them suitable for a large spectrum of applications. Up to now, most of the BPCMs have been incorporated into inorganic matrices with only a few attempts to set the BPCMs into bio-matrices. The current paper is the first comprehensive review on BPCMs incorporation in wood and wood-based materials, as renewable and sustainable materials in buildings, to enhance the thermal mass in the environmentally-friendly buildings. In the paper, the aspects of choosing BPCMs, bio-based matrices, phase change mechanisms and their combination, interpretation of life cycle analyses, and the eventual challenges of using these materials are presented and discussed.

A novel method for the acetylation of wood was investigated and compared with the classical method based on acetic anhydride. The transesterification reaction between vinyl acetate (VA) and hydroxyl groups of maritime pine sapwood (Pinus pinaster Soland) was performed in the presence of potassium carbonate as a catalyst and led to acetylated wood in high yield. The transesterification reaction was confirmed by FTIR and ¹³C CP-MAS NMR spectroscopy. The efficiency of the VA transesterification increased with increasing temperature, reaction time, and catalyst amount, but a significant weight percentage gain (WPG) was obtained after only 3 h at 90°C.