In the friction stir welding (FSW) of ultra-thin dissimilar metal sheets, different physical material properties, the reduction of plastic metal in the weld zone, and insufficient plastic metal flow lead to poor weld seam shapes and joint qualities. Therefore, it is necessary to study the flow behavior during the FSW of ultrathin sheets. In this study, micro friction stir welding (μFSW) was conducted and analyzed for the butt welding of 0.6-mm-thick ultrathin brass (H62-H) and pure copper (T2-Y) sheets. By analyzing the electric signals of the temperature and force during the welding process, testing the mechanical properties, and analyzing the metallography of the joint, the influences of the process parameters on the metal flow behavior during μFSW were studied. In the proper process conditions, the material preferentially migrated and concentric vortex flow occurred in the vicinity of the shoulder and tool pin action areas. The copper was pushed from the retreating side (RS) to the advancing side (AS) of the weld, allowing it to flow more fully. A mixture of both materials formed at the bottom of the weld nugget, and less migration occurred in the heat-affected zone of the AS at this time. The highest tensile strength can reach 194 MPa, accounting for 82.6% of the copper. The presence of brittle phases Cu₅Zn₈, AgZn₃ and AgZn caused the hardness to fluctuate slightly.

The welding tool is the key of micro friction stir welding (μFSW), which affects the heat input and the plastic forming of weld metal. In this paper, 0.8-mm-thick ultra-thin 1060-H24 aluminum sheets μFSW butt joints were used to compare and analyze the influence of the conventional tool and shoulderless tool on weld shaping, microstructure and mechanical properties. Besides, by measuring the axial force, transverse force and weld temperature in μFSW process, the influence of these two different tools on the heat input and metal flow mechanism of the weld were analyzed. The results show that the weld generated by the shoulderless tool has narrower width, less heat input and metal involved in plastic forming resulting in smaller HAZ (heat affected zone). The hardness of NZ (nugget zone) is obviously increased compared with that of the base metal. The highest tensile strength can reach 108.6 MPa, accounting for 78.6% of the base metal and 117.3% of the joint by the conventional tool. But the welding defects have to be overcome for industrial application of the shoulderless tool.