A new co-processed, rice starch-based excipient (CS) was developed via a spray-drying technique. Native rice starch (RS) was suspended in aqueous solutions of 10%–15% cross-linked carboxymethyl rice starch (CCMS) and 0.5%–6.75% silicon dioxide (in the form of sodium silicate), before spray drying. The resulting CSs were obtained as spherical agglomerates, with improved flowability. The compressibility study revealed an improved plastic deformation profile of RS, leading to better compaction and tensile strength. The presence of CCMS also ensured a rapid disintegration of the compressed tablets. CS-CCMS:SiO₂ (10:2.7), prepared with 10% CCMS, 2.7% silicon dioxide, and 40% solid content, was found to exhibit the best characteristics. Compared to the two commercial DC excipients, Prosolv^® and Tablettose^®, the flow property of CS-CCMS:SiO₂ (10:2.7) was not significantly different, while the tensile strength was 23%: lower than that of Prosolv^® but 4 times higher than that of Tablettose^® at 196 MPa compression force. The disintegration time of CS-CCMS:SiO₂ (10:2.7) tablet (28 s) was practically identical to that of Tablettose^® tablet (26 s) and far superior to that of Prosolv^® tablet (>30 min). These results show that CSs could potentially be employed as a multifunctional excipient for the manufacturing of commercial tablets by DC.

Crosslinked carboxymethyl rice starch (CLCMRS), prepared via dual modifications of native rice starch (NRS) with chloroacetic acid and sodium trimetaphosphate, was employed to facilitate the disintegration of hydroxypropylmethylcellulose (HPMC) orodispersible films (ODFs), with or without the addition of glycerol. Fabricated by using the solvent casting method, the composite films, with the HPMC--LCMRS ratios of 9:1, 7:1, 5:1 and 4:1, were then subjected to physicochemical and mechanical evaluations, including weight, thickness, moisture content and moisture absorption, swelling index, transparency, folding endurance, scanning electron microscopy, Fourier transform infrared spectroscopy, tensile strength, elongation at break, and Young’s modulus, as well as the determination of disintegration time by using the Petri dish method (PDM) and slide frame and bead method (SFM). The results showed that HPMC-CLCMRS composite films exhibited good film integrity, uniformity, and transparency with up to 20% CLCMRS incorporation (4:1 ratio). Non-plasticized composite films showed no significant changes in the average weight, thickness, density, folding endurance (96–122), tensile strength (2.01–2.13 MPa) and Young’s modulus (10.28–11.59 MPa) compared to HPMC film (135, 2.24 MPa, 10.67 MPa, respectively). On the other hand, the moisture content and moisture absorption were slightly higher, whereas the elongation at break (EAB; 4.31–5.09%) and the transparency (4.73–6.18) were slightly lowered from that of the HPMC film (6.03% and 7.03%, respectively). With the addition of glycerol as a plasticizer, the average weight and film thickness increased, and the density decreased. The folding endurance was improved (to >300), while the transparency remained in the acceptable range. Although the tensile strength of most composite films decreased (0.66–1.75 MPa), they all exhibited improved flexibility (EAB 7.27–11.07%) while retaining structural integrity. The disintegration times of most composite films (PDM 109–331, SFM 70–214 s) were lower than those of HPMC film (PDM 345, SFM 229 s). In conclusion, the incorporation of CLCMRS significantly improved the disintegration time of the composite films whereas it did not affect or only slightly affected the physicochemical and mechanical characteristics of the films. The 5:1 and 4:1 HPMC:CLCMRS composite films, in particular, showed promising potential application as a film base for the manufacturing of orodispersible film dosage forms.

A co-processed, rice starch-based excipient (CS), previously developed and shown to exhibit good pharmaceutical properties, is investigated as an all-in-one excipient for direct compression (DC). An SeDeM-ODT expert system is applied to evaluate the formulation containing CS, in comparison with those containing the physical mixture and the commercial DC excipients. The results revealed that CS showed acceptable values in all six incidence factors of the SeDeM-ODT diagram. In addition, the comprehensive indices (IGC and IGCB) were higher than 5.0, which indicated that CS could be compressed with DC technique without additional blending with a disintegrant in tablet formulation. The formulation study suggested that CS can be diluted up to 60% in the formulation to compensate for unsatisfactory properties of paracetamol. At this percentage, CS-containing tablets exhibited narrow weight variation (1.5%), low friability (0.43%), acceptable drug content (98%), and rapid disintegration (10 s). The dissolution profile of CS displayed that more than 80% of the drug content was released within 2 min. The functionality of CS was comparable to that of high functionality excipient composite (HFEC), whereas other excipients were unsuccessful in formulating the tablets. These results indicated that CS was a suitable all-in-one excipient for application in DC of tablets.

A large quantity of longan fruits (Dimocarpus longan Lour.) produced annually are processed into many products, one of which is black longan, from which the dried, dark-brown meat has been used medicinally in traditional medicine, while the starch-containing seeds are discarded. In this study, starch samples (BLGSs) were isolated from seeds of black longan fruits prepared using varied conditions. The in vitro digestibility was determined in comparison with those extracted from fresh (FLGS) and dried (DLGS) seeds. Scanning electron microscopy (SEM), X-ray diffraction (XRD), differential scanning calorimetry (DSC), and Fourier transform infrared (FTIR) spectroscopy were employed to evaluate the starch properties. The results showed that the yields of FLGS, DLGS, and BLGSs were 20%, 23%, and 16–22% w/w, respectively. SEM images showed starch granules of mixed shapes, with sizes up to 15 µm in all samples. XRD patterns confirmed an A-type crystallinity for FLGS and DLGS, with strong refraction peaks at 2θ = 15°, 17°, 18°, and 23°, while BLGSs also showed detectable peaks at 2θ = 10° and 21°, which suggested V-type structures. Thermal properties corroborated the changes by showing increases in peak gelatinization temperature (T_p) and enthalpy energy (ΔH) in BLGSs. The paste viscosity of BLGSs (5% w/w) decreased by 20–58% from that of FLGS. The FTIR peak ratio at 1045/1022 and 1022/995 cm⁻¹ also indicated an increase in ordered structure in BLGSs compared to FLGS. The significant increase in the amounts of slowly digestible starch (SDS) and resistant starch (RS) in BLGSs compared to FLGS, especially at a prolonged incubation time of 20 (4.2×) and 30 days (4.1×), was proposed to be due to the heat-induced formation of starch inclusion with other components inside the seed during the black longan production process. Thus, black longan seed could be a new source of starch, with increased RS content, for potential use in the food and related industries.

The rice bran and rice bran wax of the KJ CMU107 rice strain were investigated as potential tablet lubricants in a directly compressed tablet formulation. Stabilized full-fatted rice bran (sFFRB), stabilized defatted rice bran (sDFRB), and rice bran wax (RBW) extracted and purified from crude rice bran oil (cRBO) were tested. Two commercial lubricants, including magnesium stearate (MGS) and hydrogenated cottonseed oil (HVO), were employed as the standards in the formulated mixtures, which contained spray-dried rice starch (SDRS) as a diluent. The tableting was carried out for each formulation, and the obtained tablets were physically and mechanically evaluated. Among the parameters investigated were the general appearance, ejection force, weight variation, hardness, friability, and disintegration time. The powder flow was also determined for each formulation. The results showed that the tablet ejection forces for all the lubricated formulations (58–259 N) were significantly lower than that of the non-lubricated control formulation (349 N). The use of sFFRB as a lubricant at 0.5–2.0% w/w could lower the ejection force up to 78%, but the hardness reduced so drastically that the formulations failed the friability test due to the chipping of the tablets’ edges. Moreover, sDFRB performed significantly better as the use at 0.5–1.0% w/w in the formulation helped to lower the ejection forces by up to 80% while maintaining the changes in the tablet hardness within 10%. RBW functioned effectively as a tablet lubricant at a concentration of 0.5% w/w, yielding tablets with good strength comparable to standard HVO lubricant while helping to reduce the ejection force by 82%. In formulations with good lubrication, i.e., friability < 1%, the powder flow was improved, and the tablet disintegration times were within the same range as the control and HVO formulations. In conclusion, sDFRB displayed a lubricant property at concentrations between 0.5 and 1.0% w/w, with slightly negative effects on the tablet hardness. RBW from KJ CMU107 rice was an effective tablet lubricant at 0.5% w/w, with no effect on tablet hardness. Both materials can be further developed for use as commercial lubricants in direct compression.