The observation of nanoscale deformation in real time is a significant step toward understanding the mechanisms of friction and lubrication. Our experimental setup of a micromachine combined with a transmission electron microscope allowed us to measure the deformation, force and cross-sectional area of a single Ag asperity during shear testing. The experimental results provided insight into one of the parameters that determines the frictional coefficient. Furthermore, we demonstrated that the energy loss associated with a shear fracture event is strongly correlated with the increase in total surface energy of the two surfaces formed here after the fracture of the nanocontact.

Dislocation is a lattice imperfection of crystalline materials. Dislocation movement is induced during plastic deformation and influences the mechanical properties. Although the role of dislocation in mechanical properties has been well understood, the role of dislocation in electrical properties is completely lacking. Only Matthiessen's rule addresses the electrical influence of dislocations at the macroscale. Here, we show that the electrical conductance change due to dislocations and show their movements through in situ observation of a gold nanocontact. The density of the dislocations in the gold nanocontact did not affect the electrical conductance. The repeated and discrete dislocation movements resulted in an electrical conductance oscillation. Our results demonstrate how dislocations and their movements affect electric conductance at the nanoscale. This instability issue will cause a big problem for future electric devices such as ultra low power electric devices and nanowire photovoltaic devices.

We used inclined lithography to fabricate a pneumatic microvalve for tall microchannels such as those used to convey large cells. The pneumatic microvalve consists of three layers. The upper layer is the actual liquid microchannel, which has a parallelogram-shaped cross section of width 500 μm, height 100 μm, and an acute angle of 53.6°. The lower layer is a pneumatic microchannel that functions as an actuator, and the middle layer is a thin polydimethylsiloxane membrane between the upper and lower layers. The operation of the pneumatic microchannel actuator causes the thin membrane to bend, resulting in the bending of the liquid microchannel and its closure. It was confirmed that the closure of the liquid microchannel completely stopped the flow of the HeLa cell suspension that was used to demonstrate the operation of the microvalve. The HeLa cells that passed through the microchannel were also observed to retain their proliferation and morphological properties.

The plasticity of covalently bonded materials is a subject at the forefront of materials science, bearing on a wide range of technological and fundamental aspects. However, covalent materials fracture in a brittle manner when the deformation exceeds just a few per cent. It is predicted that a macroscopically brittle material like silicon can show nanoscale plasticity. Here we report the exceptional plasticity observed in silicon nanocontacts ('nanobridges') at room temperature using a special experimental setup combining a transmission electron microscope and a microelectromechanical system. When accounting for surface diffusion, we succeeded in elongating the nanocontact into a wire-like structure, with a fivefold increase in volume, up to more than twenty times the original length. Such a large plasticity was caused by the stress-assisted diffusion and the sliding of the intergranular, amorphous-like material among the nanocrystals.