Objective: The aim of this in vitro study was to evaluate the marginal sealing ability of a bulk fill flowable resin composite on both enamel and dentin substrates. Materials and Methods: 48 non-carious molars were selected and four Class-V cavities were prepared at the CEJ of each sample. Cavities were filled with Venus Diamond (Heraeus Kulzer); Venus Diamond Flow (Heraeus Kulzer) and Surefil SDR (Dentsply). Samples were divided into two groups: First group samples were immersed in a methylene blue solution for 30 min at 25°C. Second group samples were artificially aged and then treated with methylene blue. Samples were sectioned in the center of the restoration and observed with a 40x stereomicroscope, and the percentage of cavity infiltration was calculated. Results: Results were analyzed statistically by ANOVA (P < 0.05). The amount of infiltration was significantly lower for the enamel substrate compared with dentin (P = 0.0001) and in samples immediately immersed in methylene blue compared with those that were artificially aged (P = 0.011). The interaction between the composite material and the marginal substrate significantly affected dye penetration (P = 0.006). Conclusions: Bulk fill flowable resins provided significantly better marginal seal in dentin, both before and after artificial ageing. Nanohybrid resin composites and bulk fill flowable resins showed similar microleakage values at enamel margins. Bulk fills flowable resins provided significantly better marginal seal in dentin, both before and after artificial ageing. Nanohybrid resin composites and bulk fill flowable resins showed similar microleakage values at enamel margins.

The aim of this in vitro study was to evaluate the hardness and shrinkage stress (SS) of six bulk-fill resin composites. To evaluate microhardness (MH), ten 6 mm specimens were prepared using a metal mold for each selected bulk-fill resin composite and irradiated from the top side for 40 s using an LED light. After 24 h of storage, Vickers MH was evaluated on the upper, lower and lateral sides of the specimens. SS evaluation was then performed with a universal machine, which evaluated the contraction force generated by a bulk-fill composite specimen placed between two metal cylinders during and after light curing. The results were evaluated with a one-way ANOVA test with a post-hoc Bonferroni test and linear regression analysis (p < 0.05). All materials showed a significant MH decrease between the top and bottom surfaces. However, the bulk-fill materials tested performed differently when considering lateral depth progression. ANOVA tests for SS evaluation showed that both SDR and Venus Bulk Fill had significantly lower stress during irradiation than other tested materials. Further, MH decrease became significantly lower from the top surface at different depths in each tested group. Among the different resins, Venus Bulk Fill and SDR showed not only inferior hardness, but also a significant reduction in SS.