High-entropy oxides based on transition metals, such as Mg_0.2Co_0.2Ni_0.2Cu_0.2Zn_0.2O (TM-HEO), have recently drawn special attention as potential anodes in lithium-ion batteries due to high specific capacity and cycling reversibility. However, the lithiation/delithiation mechanism of such systems is still controversial and not clearly addressed. Here, we report on an operando XAS investigation into TM-HEO-based anodes for lithium-ion cells during the first lithiation/delithiation cycle. This material showed a high specific capacity exceeding 600 mAh g^–1 at 0.1 C and Coulombic efficiency very close to unity. The combination of functional and advanced spectroscopic studies revealed complex charging mechanisms, developing through the reduction of transition-metal (TM) cations, which triggers the conversion reaction below 1.0 V. The conversion is irreversible and incomplete, leading to the final collapse of the HEO rock-salt structure. Other redox processes are therefore discussed and called to account for the observed cycling behavior of the TM-HEO-based anode. Despite the irreversible phenomena, the HEO cubic structure remains intact for ∼60% of lithiation capacity, so proving the beneficial role of the configuration entropy in enhancing the stability of the HEO rock-salt structure during the redox phenomena.

The mechanisms of CO oxidation on the Mg0.2Co0.2Ni0.2Cu0.2Zn0.2O high entropy oxide were studied by means of operando soft X-ray absorption spectroscopy. We found that Cu is the active metal, and that Cu(II) can be rapidly reduced to Cu(I) by CO when the temperature is larger than 130 °C. Co and Ni do not have any role in this respect. The Cu(II) oxidation state can be easily but slowly recovered by treating the sample in O2 at ca. 250 °C. However, it should be noted that CuO is readily and irreversibly reduced to Cu(I) if treated in CO at T>100 °C. Thus, the main conclusion of this work is that the high configurational entropy of Mg0.2Co0.2Ni0.2Cu0.2Zn0.2O stabilizes the rock-salt structure and permits the oxidation/reduction of Cu to be reversible, thus permitting the catalytic cycle to take place.

The most common MXene composition Ti₃C₂T_x (T = F, O) shows outstanding stability as anode for sodium ion batteries (100% of capacity retention after 530 cycles with charge efficiency >99.7%). However, the reversibility of the intercalation/deintercalation process is strongly affected by the synthesis parameters determining, in turn, significant differences in the material structure. This study proposes a new approach to identify the crystal features influencing the performances, using a structural model built with a multitechnique approach that allows exploring the short-range order of the lamella. The model is then used to determine the long-range order by inserting defective elements into the structure. With this strategy it is possible to fit the MXene diffraction patterns, obtain the structural parameters including the stoichiometric composition of the terminations (neutron data), and quantify the structural disorder which can be used to discriminate the phases with the best electrochemical properties.