Airborne wear particle emission has been investigated in a pin-on-disc tribometer equipped with particle analysis equipment. The pins are cut out from commercial powder metallurgy automotive brake pads as with and without copper content. The discs are cut out from a commercial grey cast iron automotive brake disc as cut out and as in addition to a laser cladded with a powder mix of Ni-self fluxing alloy + 60% spheroidized fused tungsten carbide and then fine-ground. Dry sliding wear testing runs under a contact pressure of 0.6 MPa, sliding velocity of 2 m/s and a total sliding distance of 14,400 m. The test results show both wear and particle emission improvement by using laser cladded discs. The laser cladded discs in comparison to the reference grey cast iron discs do not alter pin wear substantially but achieves halved mass loss and quartered specific wear. Comparing in the same way, the friction coefficient increases from 0.5 to 0.6, and the particle number concentration decreases from over 100 to some 70 (1/cm³) and the partition of particles below 7 µm is approximately halved.

The tribology of an open system at temperatures ranging between 3 °C and −35 °C, with and without snow, was investigated using a pin-on-disc tribometer mounted in a temperature-controlled environmental chamber. The relationship between the microstructure and ductility of the materials and the tribology at the contacting surfaces was investigated. The study shows that during continuous sliding, pressure causes snow particles to melt into a liquid-like layer, encouraging the generation of oxide flakes on the contact path. The friction coefficient and wear rate are dramatically reduced through an oxidative friction and wear mechanism. In the absence of snow, the tribological process is controlled by the low temperature brittleness of steel in the temperature range from 3 °C to −15 °C. At these temperatures, cracks are prone to form and extend on the worn surfaces, resulting in the spalling of bulk scraps, which are crushed into debris that increases the friction coefficient and wear rate due to strong abrasion. When the temperature falls to −25 °C, an ice layer condenses on the metal surfaces and relaxes the tribological process in the same way as the added snow particles, which significantly decreases the friction and wear.