A multifunctional magneto-plasmonic CoFe₂O₄@Au core-shell nanoparticle was developed by iterative-seeding based method. This nanocargo consists of a cobalt ferrite kernel as a core (Nk) and multiple layers of gold as a functionalizable active stratum, (named as Nk@A after fifth iteration). Nk@A helps in augmenting the physiological stability and enhancing surface plasmon resonance (SPR) property. The targeted delivery of Doxorubicin using Nk@A as a nanopayload is demonstrated in this report. The drug release profile followed first order rate kinetics optimally at pH 5.4, which is considered as an endosomal pH of cells. The cellular MR imaging showed that Nk@A is an efficient T₂ contrast agent for both L6 (r₂-118.08 mM⁻¹s⁻¹) and Hep2 (r₂-217.24 mM⁻¹s⁻¹) cells. Microwave based magnetic hyperthermia studies exhibited an augmentation in the temperature due to the transformation of radiation energy into heat at 2.45 GHz. There was an enhancement in cancer cell cytotoxicity when hyperthermia combined with chemotherapy. Hence, this single nanoplatform can deliver 3-pronged theranostic applications viz., targeted drug-delivery, T₂ MR imaging and hyperthermia.

In this paper we report on the influence of polysaccharides’ molecular structure on the antibacterial activity and cytotoxicity of composites based on silver nanoparticles (AgNPs) immobilized into carboxymethyl-cellulose (CMC). These composites were green synthesized from the reduction of silver ions into aqueous solutions of the polysaccharide, using CMC with different degree of substitution (DS) and molecular weight (Mw). The composites were characterized by transmission electron microscopy (TEM), as well as infrared (ATR-FTIR), ultraviolet (UV-Vis), Raman, and X-ray photo-electron (XPS) spectroscopic techniques. The antibacterial activity was evaluated with minimum inhibitory concentration against Enterococcus faecalis. The cytotoxicity of composites was assessed against human gingival fibroblast. Experimental evidence suggests that particle size distribution and morphology of AgNPs change according to the quantity of silver precursor added to the reaction, as well as the DS and Mw of CMC used for composites preparation. This is related to the dispersion of silver precursor into aqueous solutions of the polysaccharide and the formation of Ag-O coordination bonds among AgNPs and COO⁻ moieties of CMC. Moreover, these coordination bonds modify the ability of nanoparticles to produce and release Ag⁺ into aqueous dispersion, adjusting their antibacterial activity and the induction of cytotoxicity into the tested biological environments.

In this contribution, a totally ecofriendly synthesis of silver nanoparticles from aqueous dissolution of polysaccharides is reported. The synthesis of nanoparticles was performed using aqueous dissolutions of silver nitrate (AgNO₃) and carboxymethyl-cellulose (CMC) as both reducing and stabilization agent and using different AgNO₃ : CMC weight ratios. Resultant yellowish to reddish dispersions were characterized by means of transmission electron microscopy and their related techniques, such as bright field and Z-contrast imaging and electron diffraction, as well as ultraviolet-visible and infrared spectroscopic techniques. The experimental evidence suggests that the morphology and particle size distribution of the silver nanoparticles depend on the AgNO₃ : CMC weight ratio. This feature seems to be related to the stabilization given by the CMC matrix, which, according to our experimental findings, is steric in nature. Regarding such experimental evidence, a synthesis mechanism in which CMC acts as stabilizer and reducing agent is proposed.