This study examines the influence of raw material characteristics, methods of shaping and of parameters of firing process of clay bricks, on pore-size distribution and on resistance to freeze–thaw cycles (with particular emphasis on the retention time of the specimens at the maximum achieved temperature). Pore-size distribution was measured by mercury-intrusion porosimetry, while the resistance to freeze–thaw cycles was assessed by exposing the bricks to freeze–thaw cycles (HRN B.D8.011 standard) monitoring the appearance of surface changes, decrease of compressive strength as well as the Maage factor. A correlation was set up between the Maage factor and the ratio of the compressive strength before and after freezing as a quantitative indicator of bricks resistance to frost. By using this correlation for all the examined bricks, regardless of their raw material and shaping procedure, a low coefficient of correlation (R² = 0.26) was obtained. When processed separately, machine-made bricks had a significantly higher correlation coefficient value (R² = 0.60) than the hand-made bricks (R² = 0.28).

The phenomenon of heterogeneous photocatalysis takes place in the degradation process of many organic contaminants on solid surfaces. Photocatalysis is based on the excitation of the semiconductor by irradiation with supraband gap photons and the migration of electron-hole pairs to the surface of the photocatalysts, leading to the reaction of the holes with adsorbed H₂O and OH⁻ to form hydroxyl radicals. Due to the stability and photosensitivity of TiO₂ semiconductors, this system is well studied and is of great interest from an ecological and industrial point of view for use in the field of building materials. Clay roofing tiles, due to their long-term exploitation, are subject to physical, chemical and biological degradation that leads to deterioration. Ceramic systems have a high percentage of total porosity and considering their non-tolerance of organic coating, the use of surface active materials (SAM) that induce porosity in TiO₂ coatings is of vital significance. Photocatalytic coatings applied on clay roofing tiles under industrial conditions were designed by varying the quantity of TiO₂ (mass/cm²) on the tile surface (thin and thick TiO₂ layer). The positive changes in specific surface area and mesopore structure of the designed coatings were made by the addition of PEG 600 as a surface active material. It was shown that a thin photocatalytic layer (0.399 mg suspension/cm² tile surface), applied onto ceramic tiles under industrial conditions, had better photocatalytic activity in methylene blue decomposition, hydrophilicity and antimicrobial activity than a thick photocatalytic coating (0.885 mg suspension/cm²).